Polimeri Europa Sinkral® PD L 322 ABS Resin

Category	Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer	Polimeri Europa (Former EniChem)
Trade Name	Sinkral®
Port	Shanghai port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	Polimeri Europa Sinkral® PD L 322 ABS Resin.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Sinkral PD L 322 by continuous mass, is a general purpose, high flow injection molding grade having good impact resistance coupled with an excellent gloss.Applications: Widely used in the small and large household appliance sector, vacuum cleaners, toys, telephones and consumer electronics.Information provided by Polimeri Europa.

Physical Properties	Metric	English	Comments
Specific Gravity	1.04 g/cc	1.04 g/cc	ISO 1183
Water Absorption	0.30 % <br>@Time 86400 sec	0.30 % <br>@Time 24.0 hour	ASTM D570
Melt Flow	23 g/10 min <br>@Load 10.0 kg,<br> Temperature 220 °C	23 g/10 min <br>@Load 22.0 lb,<br> Temperature 428 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	109	109	ISO 2039/2
Tensile Strength at Break	45.0 MPa	6530 psi	ASTM D638
Elongation at Break	20 %	20 %	ASTM D638
Flexural Strength	69.0 MPa	10000 psi	ASTM D790
Flexural Modulus	2.35 GPa	341 ksi	ASTM D790
Izod Impact, Notched	0.500 J/cm <br>@Thickness 3.20 mm,<br> Temperature -40.0 °C	0.937 ft-lb/in <br>@Thickness 0.126 in,<br> Temperature -40.0 °F	ISO 180/4A
	0.700 J/cm <br>@Thickness 3.20 mm,<br> Temperature -20.0 °C	1.31 ft-lb/in <br>@Thickness 0.126 in,<br> Temperature -4.00 °F	ISO 180/4A
	1.00 J/cm <br>@Thickness 3.20 mm,<br> Temperature 0.000 °C	1.87 ft-lb/in <br>@Thickness 0.126 in,<br> Temperature 32.0 °F	ISO 180/4A
	1.70 J/cm <br>@Thickness 3.20 mm,<br> Temperature 23.0 °C	3.18 ft-lb/in <br>@Thickness 0.126 in,<br> Temperature 73.4 °F	ISO 180/4A
Izod Impact, Notched (ISO)	6.00 kJ/m² <br>@Thickness 4.00 mm,<br> Temperature -40.0 °C	2.86 ft-lb/in² <br>@Thickness 0.157 in,<br> Temperature -40.0 °F	ISO 180/1A
	13.0 kJ/m² <br>@Thickness 4.00 mm,<br> Temperature 23.0 °C	6.19 ft-lb/in² <br>@Thickness 0.157 in,<br> Temperature 73.4 °F	ISO 180/1A
Charpy Impact Unnotched	NB <br>@Temperature 23.0 °C	NB <br>@Temperature 73.4 °F	DIN 53453
	NB <br>@Temperature -40.0 °C	NB <br>@Temperature -40.0 °F	DIN 53453
Charpy Impact, Notched	0.900 J/cm² <br>@Temperature 23.0 °C	4.28 ft-lb/in² <br>@Temperature 73.4 °F	DIN 53453

Thermal Properties	Metric	English	Comments
CTE, linear	90.0 µm/m-°C	50.0 µin/in-°F	ASTM D696
Thermal Conductivity	0.170 W/m-K	1.18 BTU-in/hr-ft²-°F	ASTM C177
Vicat Softening Point	96.0 °C <br>@Load 5.10 kg	205 °F <br>@Load 11.2 lb	ISO 306/B 120
	99.0 °C <br>@Load 1.02 kg	210 °F <br>@Load 2.25 lb	ISO 306/A 120
Flammability, UL94	HB <br>@Thickness 1.50 mm	HB <br>@Thickness 0.0591 in
Glow Wire Test	650 °C <br>@Thickness 3.00 mm	1200 °F <br>@Thickness 0.118 in	IEC 60695-2-1
Shrinkage	0.40 - 0.60 %	0.40 - 0.60 %	Internal method

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+16 ohm-cm	1.00e+16 ohm-cm	IEC 60093
Surface Resistance	1.00e+15 ohm	1.00e+15 ohm	IEC 60093
Dielectric Constant	3.1 <br>@Frequency 1000 Hz	3.1 <br>@Frequency 1000 Hz	dry; IEC 60250
Dielectric Strength	30.0 kV/mm	762 kV/in	IEC 60243
Dissipation Factor	0.015 <br>@Frequency 1000 Hz	0.015 <br>@Frequency 1000 Hz	dry; IEC 60250