Polimeri Europa Edistir N 2380 Polystyrene

Category Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Molded, Unreinforced
Manufacturer Polimeri Europa (Former EniChem)
Trade Name Edistir
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa Edistir N 2380 Polystyrene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High molecular weight general purpose polystyrene combining high heat resistance and good mechanical strength. Suitable for direct gassing extrusion, for biaxially oriented films and sheets, for glass clear sheets and panels. Also used in injection molding of medium thick wall transparent parts.Designation: Thermoplastics ISO 1622-PS,G,105-03Applications: Uses range from foamed packaging trays, clear panels for shower cabins, insulation boards (XPS), OPS for labels and packaging to moulded fridge clear components, Petri dishes, technical parts.N 2380 is certified UL94 HB "all colors" at 1.5 mm (UL file E83071). This grade in its natural version complies by composition with the requirements set by the main Regulations for plastic materials intended for food contact (including the EEC Directive 90/128 and subsequent amendments).Information provided by Polimeri Europa
Physical Properties Metric English Comments
Bulk Density 0.650 g/cc
0.0235 lb/in³
ISO 60
Density 1.05 g/cc
0.0379 lb/in³
ISO 1183
Water Absorption <= 0.10 %
<= 0.10 %
24 hours - 23°C; ISO 62
Linear Mold Shrinkage 0.0030 - 0.0060 cm/cm
0.0030 - 0.0060 in/in
Internal Method
Melt Flow 2.0 g/10 min

@Load 5.00 kg,
Temperature 200 °C
2.0 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 80
80
ISO 2039/2
Tensile Strength at Break 49.0 MPa
7110 psi
5 mm/min; ISO 527
Elongation at Break 2.5 %
2.5 %
5 mm/min; ISO 527
Tensile Modulus 3.35 GPa
486 ksi
1 mm/min; ISO 527
Flexural Strength 91.0 MPa
13200 psi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 1.70 kJ/m²

@Thickness 4.00 mm,
Temperature -30.0 °C
0.809 ft-lb/in²

@Thickness 0.157 in,
Temperature -22.0 °F
ISO 180/1A
1.90 kJ/m²

@Thickness 4.00 mm,
Temperature 23.0 °C
0.904 ft-lb/in²

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180/1A
Thermal Properties Metric English Comments
CTE, linear 70.0 µm/m-°C

@Temperature 20.0 °C
38.9 µin/in-°F

@Temperature 68.0 °F
ASTM D 696
Thermal Conductivity 0.170 W/m-K
1.18 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 1.8 MPa (264 psi) 95.0 °C
203 °F
120°C/h; ASTM D 648
Vicat Softening Point 101 °C
214 °F
50 N - 50°C/h; ISO 306/B
106 °C
223 °F
10 N - 50°C/h; ISO 306/A
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
UL94
Glow Wire Test 650 °C

@Thickness 1.60 mm
1200 °F

@Thickness 0.0630 in
IEC 60695-2-1
Optical Properties Metric English Comments
Transmission, Visible 90 %
90 %
transparent; thickness not quantified
Electrical Properties Metric English Comments
Volume Resistivity 7.00e+15 ohm-cm
7.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.50e+15 ohm
1.50e+15 ohm
IEC 60093
Dielectric Constant 2.5

@Frequency 50 Hz
2.5

@Frequency 50 Hz
IEC 60250
Dielectric Strength 70.0 kV/mm
1780 kV/in
IEC 60243
Dissipation Factor 0.00020

@Frequency 50 Hz
0.00020

@Frequency 50 Hz
IEC 60250
Comparative Tracking Index 425 V
425 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 210 - 240 °C
410 - 464 °F
Extrusion
220 - 270 °C
428 - 518 °F
Injection Molding
Mold Temperature 20.0 - 60.0 °C
68.0 - 140 °F
Injection Molding