PlastiComp Complet® LGF60 - PA6 Nylon 6, 60% Long Glass Fiber Reinforced

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 60% Glass Fiber Filled
Manufacturer	PlastiComp
Trade Name	Complēt®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PlastiComp Complet® LGF60 - PA6 Nylon 6, 60% Long Glass Fiber Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Complet® long-fiber reinforced pellets are manufactured to exceed expectation for quality and performance.Nylon 6 with 60% long glass reinforcementInformation provided by PlastiComp, Inc.

Physical Properties	Metric	English	Comments
Specific Gravity	1.69 g/cc	1.69 g/cc	ASTM D-792
Filler Content	60 %	60 %	Long Glass Fiber

Mechanical Properties	Metric	English	Comments
Tensile Strength	228 MPa	33100 psi	ASTM D-638
Elongation at Break	1.0 - 2.0 %	1.0 - 2.0 %	ASTM D-638
Tensile Modulus	20.0 GPa	2900 ksi	ASTM D-638
Flexural Strength	359 MPa	52100 psi	ASTM D-790
Flexural Modulus	21.379 GPa	3100.8 ksi	ASTM D-790
Izod Impact, Notched	3.74 J/cm	7.01 ft-lb/in	ASTM D-256
Izod Impact, Unnotched	14.95 J/cm	28.01 ft-lb/in	ASTM D-4812

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	221 °C	430 °F	ASTM D-648

Processing Properties	Metric	English
Rear Barrel Temperature	260 - 277 °C	500 - 530 °F
Middle Barrel Temperature	266 - 282 °C	510 - 540 °F
Front Barrel Temperature	271 - 288 °C	520 - 550 °F
Nozzle Temperature	271 - 288 °C	520 - 550 °F
Melt Temperature	271 - 288 °C	520 - 550 °F
Mold Temperature	93.3 °C	200 °F
Injection Velocity	50.8 - 76.2 mm/sec	2.00 - 3.00 in/sec
Drying Temperature	85.0 °C @Time 14400 sec	185 °F @Time 4.00 hour
Moisture Content	<= 0.18 %	<= 0.18 %
Back Pressure	0.172 - 0.345 MPa	25.0 - 50.0 psi
Cushion	0.635 cm	0.250 in
Screw Speed	30 - 50 rpm	30 - 50 rpm

Descriptive Properties	Value	Comments
Injection Pressure	Medium to maximum