- PlastiComp Complet® LCF40 - PA66 MT Nylon 66, 40% Long Carbon Fiber Reinforced, Impact Modified
PlastiComp Complet® LCF40 - PA66 MT Nylon 66, 40% Long Carbon Fiber Reinforced, Impact Modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Carbon Fiber Filled , Nylon 66, Impact Grade |
| Manufacturer | PlastiComp |
| Trade Name | Complēt® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PlastiComp Complet® LCF40 - PA66 MT Nylon 66, 40% Long Carbon Fiber Reinforced, Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Complēt® long-fiber reinforced pellets are manufactured to exceed expectation for quality and performance.Nylon 66 with 40% carbon fiber reinforcementImpact modifiedInformation provided by PlastiComp, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D-792 |
| Filler Content | 40 % | 40 % | Carbon Fiber |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 331 MPa | 48000 psi | ASTM D-638 |
| Elongation at Break | 1.0 - 2.0 % | 1.0 - 2.0 % | ASTM D-638 |
| Tensile Modulus | 33.793 GPa | 4901.3 ksi | ASTM D-638 |
| Flexural Strength | 483 MPa | 70100 psi | ASTM D-790 |
| Flexural Modulus | 27.586 GPa | 4001.0 ksi | ASTM D-790 |
| Izod Impact, Notched | 3.10 J/cm | 5.81 ft-lb/in | ASTM D-256 |
| Izod Impact, Unnotched | 11.748 J/cm | 22.009 ft-lb/in | ASTM D-4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D-648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 282 - 299 °C | 540 - 570 °F | |
| Middle Barrel Temperature | 288 - 304 °C | 550 - 580 °F | |
| Front Barrel Temperature | 293 - 310 °C | 560 - 590 °F | |
| Nozzle Temperature | 288 - 304 °C | 550 - 580 °F | |
| Melt Temperature | 293 - 310 °C | 560 - 590 °F | |
| Mold Temperature | 93.3 °C | 200 °F | |
| Injection Velocity | 50.8 - 76.2 mm/sec | 2.00 - 3.00 in/sec | |
| Drying Temperature | 85.0 °C @Time 14400 sec |
185 °F @Time 4.00 hour |
|
| Moisture Content | <= 0.18 % | <= 0.18 % | |
| Back Pressure | 0.172 - 0.345 MPa | 25.0 - 50.0 psi | |
| Cushion | 0.635 cm | 0.250 in | |
| Screw Speed | 30 - 50 rpm | 30 - 50 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Pressure | Medium to maximum |
Users viewing this material also viewed the following:
- Noble Polymers Regis™ 315107 Thermoplastic Olefin (TPO)
- Solvay Specialty Polymers Udel® P-1720 Polysulfone (PSU) (discontinued **)
- Ineos ABS Lustran® SAN GF20 Glass Fiber Reinforced
- IRPC Polimaxx Porene AP102 Acrylonitrile Butadiene Styrene
- Shakespeare WhisperTouch® Ultra Soft low luster, TEX# 8 Nylon Industrial Sewing Thread
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 20 PHR Non-Black, Mistron Vapor
- Ascend Performance Materials Vydyne® 50BWFS Nylon 66, General Purpose
- Bhansali Engineering Abstron IM-17 A EP ABS Electro Plating Applications
- Ascend Performance Materials Vydyne® 47H BK0668 Nylon 66, Impact Modified, Heat Stabilized, Conditioned
- Kennametal Stellite Stellite® 31 PM after P/M processing, aged 8 hours at 802°C air cooled
Copyright © lookpolymers.com All Rights Reserved