POLYMER SEARCH

Plastcom SLOVAMID 6 LI/1 Polyamide 6, Impacted

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade
Manufacturer	Plastcom spol. s r.o.
Trade Name	SLOVAMID
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Plastcom SLOVAMID 6 LI/1 Polyamide 6, Impacted.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

FeaturesPA 6 with the content of thermoplastic elastomer. Impacted, for mouldings with high toughness either at low temperatures, suitable for external use, eg. ski shoes, sports and safety helmets, protection ledges of the car-doors. Delivered in natural and in the full RAL color scale.Application: Injection MouldingInformation Provided by Plastcom spol. s r.o.

Physical Properties	Metric	English	Comments
Density	1.10 g/cc	0.0397 lb/in³	STN 64 0111
Linear Mold Shrinkage	0.0208 cm/cm	0.0208 in/in	STN 64 0808
Linear Mold Shrinkage, Transverse	0.0204 cm/cm	0.0204 in/in	STN 64 0808
Melt Flow	10 g/10 min @Load 2.16 kg, Temperature 230 °C	10 g/10 min @Load 4.76 lb, Temperature 446 °F	STN EN ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	64.0 MPa	9280 psi	STN EN ISO 527-2
Elongation at Break	4.0 %	4.0 %	STN EN ISO 527-2
Tensile Modulus	2.75 GPa	399 ksi	STN EN ISO 527-2
Flexural Strength	95.0 MPa	13800 psi	STN EN ISO 178
Flexural Modulus	2.40 GPa	348 ksi	STN EN ISO 178
Charpy Impact Unnotched	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	STN EN ISO 179
	NB @Temperature -20.0 °C	NB @Temperature -4.00 °F	STN EN ISO 179
Charpy Impact, Notched	0.800 J/cm² @Temperature -20.0 °C	3.81 ft-lb/in² @Temperature -4.00 °F	STN EN ISO 179
	1.10 J/cm² @Temperature 23.0 °C	5.23 ft-lb/in² @Temperature 73.4 °F	STN EN ISO 179

Thermal Properties	Metric	English	Comments
Melting Point	222 °C	432 °F	DSC; STN EN ISO 3146
Deflection Temperature at 1.8 MPa (264 psi)	68.0 °C	154 °F	STN EN ISO 75/A
Vicat Softening Point	218 °C	424 °F	B; STN EN ISO 306

Processing Properties	Metric	English	Comments
Melt Temperature	240 - 260 °C	464 - 500 °F
Mold Temperature	50.0 - 60.0 °C	122 - 140 °F
Drying Temperature	80.0 °C	176 °F
Dry Time	4 hour	4 hour
Moisture Content	0.20 %	0.20 %	STN EN ISO 960
Injection Pressure	80.0 - 150 MPa	11600 - 21800 psi