ExxonMobil Escorene® LD 722.MV Molding, extrusion and compounding resin  (discontinued **)

Category Polymer , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Extrusion/Coating Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Escorene® LD 722.MV Molding, extrusion and compounding resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Escorene Ultra LD 722.MV is a high vinyl acetate copolymer resin for specialty extrusion and compounding application. Articles made from LD 722.MV are soft and have excellent low temperature toughness.Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.944 g/cc
0.0341 lb/in³
ExxonMobil Method
Vinyl Acetate Content 22 %
22 %
ExxonMobil Method
Melt Flow 3.0 g/10 min
3.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore A 78
78
15s; ASTM D2240
Hardness, Shore D 32
32
15s; ASTM D2240
Tensile Strength at Break 9.58 MPa
1390 psi
ASTM D638
Elongation at Break >= 800 %
>= 800 %
ASTM D638
Flexural Modulus 0.0454 GPa
6.58 ksi
1% secant; ASTM D790
Impact Test 16.3 J

@Temperature 23.0 °C
12.0 ft-lb

@Temperature 73.4 °F
Instrument Impact, Total Energy; ASTM D3763
29.8 J

@Temperature -40.0 °C
22.0 ft-lb

@Temperature -40.0 °F
Instrumented Impact, Total Energy; ASTM D3763
Thermal Properties Metric English Comments
Melting Point 81.7 °C
179 °F
Peak Melting Temperature; ExxonMobil Method
Vicat Softening Point 57.8 °C
136 °F
ASTM D1525
Descriptive Properties Value Comments
Features Thermal Stabilizer