Plastcom SLOVAMID 6 GF 25 Polyamide 6, 25% Glass Fiber

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer Plastcom spol. s r.o.
Trade Name SLOVAMID
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastcom SLOVAMID 6 GF 25 Polyamide 6, 25% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FeaturesPA 6 for injection moulding, chemically strengthened with 25% of glass fiber, for mouldings with high strength and toughness used in the automotive, electrical, engineering and consumer-goods industry. Application: grips of electro tools, hobby tools, gears, covers of electric appliances, cooling screws of blowers, electromotors, carrying parts in the automotive industry.Application: Injection MouldingInformation Provided by Plastcom spol. s r.o.
Physical Properties Metric English Comments
Density 1.30 g/cc
0.0470 lb/in³
STN 64 0111
Linear Mold Shrinkage 0.0050 cm/cm
0.0050 in/in
STN 64 0808
Linear Mold Shrinkage, Transverse 0.0138 cm/cm
0.0138 in/in
STN 64 0808
Melt Flow 3.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
3.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
STN EN ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 140 MPa
20300 psi
STN EN ISO 527-2
Elongation at Break 3.0 %
3.0 %
STN EN ISO 527-2
Tensile Modulus 7.40 GPa
1070 ksi
STN EN ISO 527-2
Flexural Strength 200 MPa
29000 psi
STN EN ISO 178
Flexural Modulus 6.30 GPa
914 ksi
STN EN ISO 178
Charpy Impact Unnotched 2.70 J/cm²

@Temperature -20.0 °C
12.8 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
5.00 J/cm²

@Temperature 23.0 °C
23.8 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
Charpy Impact, Notched 0.700 J/cm²

@Temperature -20.0 °C
3.33 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
1.00 J/cm²

@Temperature 23.0 °C
4.76 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
DSC; STN EN ISO 3146
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
STN EN ISO 75/A
Vicat Softening Point 210 °C
410 °F
B; STN EN ISO 306
Flammability, UL94 HB
HB
Glow Wire Test 650 °C
1200 °F
STN IEC 60695-2-10
Processing Properties Metric English Comments
Melt Temperature 250 - 280 °C
482 - 536 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4 hour
4 hour
Moisture Content 0.15 %
0.15 %
STN EN ISO 960
Injection Pressure 70.0 - 120 MPa
10200 - 17400 psi