Ravago Manufacturing Americas Hylon® N1043L Nylon 6/6 (Cond) (discontinued **)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hylon® N1043L Nylon 6/6 (Cond)
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Ravago.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | DAM; ASTM D792 |
| Water Absorption | 0.60 % | 0.60 % | 24 hrs, DAM; ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | 0.125 in, DAM; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 88 | 88 | ASTM D785 |
| Tensile Strength at Break | 152 MPa | 22000 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 207 MPa | 30000 psi | ASTM D790 |
| Flexural Modulus | 6.89 GPa | 1000 ksi | ASTM D790 |
| Izod Impact, Notched | 1.71 J/cm | 3.20 ft-lb/in | 73°F; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 249 °C | 480 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB | 0.0591 in, BK |
| HB | HB | 0.118 in, BK |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 282 - 304 °C | 540 - 580 °F | |
| Mold Temperature | 65.6 - 98.9 °C | 150 - 210 °F | |
| Drying Temperature | 73.9 °C | 165 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Moisture Content | 0.20 % | 0.20 % | |
| Back Pressure | 0.138 - 0.414 MPa | 20.0 - 60.0 psi | |
| Screw Speed | 40 - 120 rpm | 40 - 120 rpm |
Users viewing this material also viewed the following:
- Proto3000 Objet Digital Materials™ DM_Dots_7513 Transparent Prototyping Polymer
- Qualchem Danamid FGFHUV-30 Polyamide 6, 30% Glass Fiber
- Chevron Phillips LX8119 HDPE Injection Molding Resin (discontinued **)
- NOVA Chemicals Novapol® PF-0218-F Butene LLDPE Film Resin
- Lanxess Durethan® BKV 115 H2.0 901510 Copolyamide, 15% Glass Fiber
- Schott Glass 8229 Intermediate sealing glass
- Fainplast Compounds GS 8202 Flexible PVC, Injection Molding for Footwear
- Albis Plastics Tedur® L 9523 PPS, 60% Glass Fiber/Mineral
- Momentive Performance Materials Ultraglaze® 4400 Construction Sealant
Copyright © lookpolymers.com All Rights Reserved