Addiplast Addinyl C2 ZV40 Nylon 66/6, 40% Glass Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 40% Glass Fiber Reinforced |
| Manufacturer | Addiplast |
| Trade Name | Addinyl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Addiplast Addinyl C2 ZV40 Nylon 66/6, 40% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Glass fiber reinforced, increased thermal aging stabilityInformation provided by Addiplast.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 79 | 79 | Conditioned; ISO 868 |
| 85 | 85 | ISO 868 | |
| Tensile Strength at Break | 130 MPa | 18900 psi | Conditioned; ISO R 527 |
| 195 MPa | 28300 psi | ISO R 527 | |
| Elongation at Yield | 3.0 % | 3.0 % | ISO R 527 |
| 6.0 % | 6.0 % | Conditioned; ISO R 527 | |
| Modulus of Elasticity | 6.10 GPa | 885 ksi | Conditioned; ISO 178 |
| 11.5 GPa | 1670 ksi | ISO 178 | |
| Izod Impact, Notched (ISO) | 16.0 kJ/m² | 7.61 ft-lb/in² | ISO 180/1A |
| 22.0 kJ/m² | 10.5 ft-lb/in² | Conditioned; ISO 180/1A | |
| Charpy Impact Unnotched | 6.50 J/cm² | 30.9 ft-lb/in² | ISO 179/IeU |
| 7.50 J/cm² | 35.7 ft-lb/in² | Conditioned; ISO 179/IeU | |
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | ISO 179/IeA |
| 1.80 J/cm² | 8.57 ft-lb/in² | Conditioned; ISO 179/IeA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C | 16.7 µin/in-°F | ASTM E831 |
| Melting Point | 243 °C | 469 °F | ISO 3146/C2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-2/AF |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Conditioned; CEI 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | CEI 60093 | |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | Conditioned; CEI 60243-1 |
| 35.0 kV/mm | 889 kV/in | CEI 60243-1 | |
| Comparative Tracking Index | 550 V | 550 V | CEI 60112/Solution A |
Users viewing this material also viewed the following:
- Pau Tai UNISTAB LCZ-240P Liquid Stabilizer for Paste Resin
- BASF Master Builders Solutions ChemRex® CX-943 Squeegee-grade Polyurethane Adhesive (discontinued **)
- Ineos A4040 HDPE
- SABIC Innovative Plastics Valox® 310SE0 PBT (Europe-Africa-Middle East)
- A. Schulman SCHULAMID® 66 GF33HS 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66
- A. Schulman PAPERMATCH® T-4228-50 Specialty Masterbatch
- Loctite® Super Bonder® 430 Instant Adhesive
- DSM Akulon® K224-LGM35 (Dry) 15% Glass Reinforced, 25% Mineral Reinforced Nylon 6 (North America)
- Braskem Green PE SLH218 Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene
Copyright © lookpolymers.com All Rights Reserved