EMS-Grivory Grivory® BGK-30 X PA6-(GF+GB)30
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced |
| Manufacturer | EMS-Grivory (EMS-CHEMIE) |
| Trade Name | Grivory® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EMS-Grivory Grivory® BGK-30 X PA6-(GF+GB)30.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by EMS Grivory
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Water Absorption | 7.0 % | 7.0 % | ISO 62 |
| Moisture Absorption | 2.00 % | 2.00 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 80.0 MPa | 11600 psi | conditioned; ISO 527-1/-2 |
| 140 MPa | 20300 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 3.0 % | 3.0 % | dry; ISO 527-1/-2 |
| 7.0 % | 7.0 % | conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 3.80 GPa | 551 ksi | conditioned; ISO 527-1/-2 |
| 7.00 GPa | 1020 ksi | dry; ISO 527-1/-2 | |
| Charpy Impact Unnotched | 6.50 J/cm² | 30.9 ft-lb/in² | dry; ISO 179/1eU |
| 7.50 J/cm² | 35.7 ft-lb/in² | conditioned; ISO 179/1eU | |
| 5.00 J/cm² @Temperature 30.0 °C |
23.8 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |
| 5.00 J/cm² @Temperature 30.0 °C |
23.8 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | dry; ISO 179/1eA |
| 1.50 J/cm² | 7.14 ft-lb/in² | conditioned; ISO 179/1eA | |
| 0.600 J/cm² @Temperature 30.0 °C |
2.86 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |
| 0.600 J/cm² @Temperature 30.0 °C |
2.86 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C | 19.4 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 |
| Maximum Service Temperature, Air | 90.0 - 110 °C | 194 - 230 °F | long term; EMS |
| 160 °C | 320 °F | short term; EMS | |
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 140 °C | 284 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB | HB | IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | conditioned; IEC 60093 |
| 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | dry; IEC 60093 | |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Strength | 23.0 kV/mm | 584 kV/in | conditioned; IEC 60243-1 |
| 29.0 kV/mm | 737 kV/in | dry; IEC 60243-1 | |
| Comparative Tracking Index | 400 V | 400 V | conditioned; IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Form | Granules | |
| Processing | Injection Molding |
Users viewing this material also viewed the following:
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 30 PHR N220 (ISAF) Filler
- Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 4.8 mm thick sheet
- Latrobe Lescalloy® AF 1410 VIM-VAR ; 13.5 in High Strength Alloy Steel
- SYNTHOS Koplen® 0513 FR Expandable Polystyrene
- Teknor Apex APEX® 3311-60 Polyvinyl Chloride, Flexible
- SABIC Innovative Plastics XYLEX X8210 PC+POLYESTER (Asia Pacific)
- Dow Nordel® IP 4640 Dense Extruded Profile
- 3M FM052R Indoor UL Recognized Brite Silver Polyester Label Products
- BASF Ultraform® S2320 0035 LEV POM
Copyright © lookpolymers.com All Rights Reserved