Permabond HM162 Anaerobic Retainer
| Category | Polymer , Adhesive , Thermoset , Acrylic/Cyanoacrylate Adhesive |
| Manufacturer | Permabond |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Permabond HM162 Anaerobic Retainer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Permabond® HM162 is a medium viscosity retaining compound that cures when confined between metal parts to form an extremely tough bond. It is best suited for cylindrical parts and where high temperature resistance is required. In the uncured, liquid state, the adhesive wets the metal surfaces, keying into all surface irregularities and fills the space between the mated parts. Features & Benefits: Rapid cure Very high strength Improved fatigue life Excellent chemical resistance Excellent temperature resistance Information provided by Permabond.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | Uncured |
| Viscosity | 1000 cP @Temperature 25.0 °C |
1000 cP @Temperature 77.0 °F |
Uncured |
| Storage Temperature | 5.00 - 25.0 °C | 41.0 - 77.0 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Adhesive Bond Strength | 30.0 MPa | 4350 psi | steel collar and pin shear; ISO 10123 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C | 50.0 µin/in-°F | |
| Thermal Conductivity | 0.190 W/m-K | 1.32 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 199 °C | 390 °F | |
| Minimum Service Temperature, Air | -53.9 °C | -65.0 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 11.0 kV/mm | 279 kV/in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 4.98 min @Temperature 23.0 °C |
0.0830 hour @Temperature 73.4 °F |
M10 steel, handling strength |
| 4.98 min @Temperature 23.0 °C |
0.0830 hour @Temperature 73.4 °F |
Brass, handling strength | |
| 7.02 min @Temperature 23.0 °C |
0.117 hour @Temperature 73.4 °F |
Zinc, handling strength | |
| 15.0 min @Temperature 23.0 °C |
0.250 hour @Temperature 73.4 °F |
Brass, working strength | |
| 30.0 min @Temperature 23.0 °C |
0.500 hour @Temperature 73.4 °F |
Stainless steel, handling strength | |
| 60.0 - 180 min @Temperature 23.0 °C |
1.00 - 3.00 hour @Temperature 73.4 °F |
M10 steel, working strength | |
| 180 min @Temperature 23.0 °C |
3.00 hour @Temperature 73.4 °F |
Zinc, working strength | |
| 1440 min @Temperature 23.0 °C |
24.0 hour @Temperature 73.4 °F |
Stainless steel, working strength | |
| 1440 min @Temperature 23.0 °C |
24.0 hour @Temperature 73.4 °F |
M10 steel, full strength | |
| 4320 min @Temperature 23.0 °C |
72.0 hour @Temperature 73.4 °F |
Zinc, full strength |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Green | Uncured |
| Maximum Gap Fill (mm) | 0.2 | |
| Strength Retention | 50% at 150°C | Relative to 0°C |
| 80% at 100°C | Relative to 0°C | |
| 93% at 50°C | Relative to 0°C | |
| Torque Strength (N m) | 32 | M10 steel, break |
| 57 | M10 steel, prevail | |
| UV Fluorescence | Yes | Uncured |
Users viewing this material also viewed the following:
- Covestro Makrolon® CD 2005 Polycarbonate, Optical/Compact Disc Grade (discontinued **)
- Grupo Repol Dinalon® B1S25 N Fast Cycling, Nucleated Nylon 6
- Karina 850-10/199-Y-ERYM White PVC Compound
- Multibase Multi-Flamâ„¢ 0206 PP Polypropylene
- Shakespeare S-3 Economy Nylon Copolymer Fishing Line, 6 lb
- EMS-Grivory Grivory® L 16 LM PA12
- 3M Jet-Weld™ TS-230 Adhesive
- Tipco Tipcolene® FPDG-M FPDG M - 28% Talc/Mineral Reinforced Polypropylene Copolymer, High Stiffness & Impact Strength
Copyright © lookpolymers.com All Rights Reserved