SABIC Innovative Plastics LNP Lubricomp RP0049 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, PTFE Filled |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Lubricomp RP0049 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* RP0049 is a compound based on Nylon 66 resin containing Flame Retardant, PTFE, Silicone. Added features of this material include: Flame Retardant.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ASTM D 792 |
| 1.49 g/cc | 0.0538 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 0.47 % @Time 86400 sec |
0.47 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.020 cm/cm @Time 86400 sec |
0.020 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.020 cm/cm @Time 86400 sec |
0.020 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.019 cm/cm @Time 86400 sec |
0.019 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0194 cm/cm @Time 86400 sec |
0.0194 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 37.0 MPa | 5370 psi | ISO 527 |
| 41.0 MPa | 5950 psi | ASTM D 638 | |
| Elongation at Break | 2.7 % | 2.7 % | ASTM D 638 |
| 3.3 % | 3.3 % | ISO 527 | |
| Tensile Modulus | 2.48 GPa | 360 ksi | 50 mm/min; ASTM D 638 |
| 2.50 GPa | 363 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 67.0 MPa | 9720 psi | ASTM D 790 |
| 68.0 MPa | 9860 psi | ISO 178 | |
| Flexural Modulus | 2.27 GPa | 329 ksi | ASTM D 790 |
| 2.40 GPa | 348 ksi | ISO 178 | |
| Izod Impact, Notched | 0.210 J/cm @Temperature 23.0 °C |
0.393 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 2.13 J/cm @Temperature 23.0 °C |
3.99 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 15.0 kJ/m² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 4.00 J @Temperature 23.0 °C |
2.95 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Coefficient of Friction, Dynamic | 0.18 | 0.18 | ASTM D 3702 Modified |
| Coefficient of Friction, Static | 0.13 | 0.13 | ASTM D 3702 Modified |
| K (wear) Factor | 12.1 x 10-8 mm³/N-M | 6.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D 3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C @Thickness 3.20 mm |
334 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 80.0 °C @Thickness 3.20 mm |
176 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Kolon KOCETAL® VT301 Anti-Static Grade Acetal Resin
- LATI Latamid SP1 G/50 PA 6.10, 50% Glass Fiber Reinforced
- SABIC Innovative Plastics Ultem ATX100R PEI+PCE (Asia Pacific)
- Thermoseal KLINGERSIL® C-4201 General Application Gasketing
- Westlake Plastics ECTFE Film Made from HALAR® Ethylene-chlorotrifluoroethylene Resin
- Chevron Phillips MarFlex® 7109DJ LLDPE Blown Film Resin
- Chosun Refractories CUN-804 Nozzle Brick
- Bulk Molding Compounds BMC 600 Mineral Filled, Glass Fiber Reinforced Polyester Compound
- Haynes 625 alloy, 10% cold reduction, 1065°C anneal for 5 minutes
Copyright © lookpolymers.com All Rights Reserved