Permabond HM135 Anaerobic Retainer

Category	Polymer , Adhesive , Thermoset , Acrylic/Cyanoacrylate Adhesive
Manufacturer	Permabond
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Permabond HM135 Anaerobic Retainer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Permabond® HM135 is a fast curing, medium viscosity anaerobic adhesive for locking and sealing threads and retaining cylindrical components. It gives maximum torque strength on brass or plated brass components and provides excellent temperature and chemical resistance. Features & Benefits: Very high strength Rapid cure Suitable for use with non-ferrous metals High temperature resistance Excellent chemical resistance WRAS listed for contact with wholesome (potable) water Information provided by Permabond.

Physical Properties	Metric	English	Comments
Specific Gravity	1.10 g/cc	1.10 g/cc	Uncured
Viscosity	700 cP @Temperature 25.0 °C	700 cP @Temperature 77.0 °F	Uncured
Storage Temperature	5.00 - 25.0 °C	41.0 - 77.0 °F

Mechanical Properties	Metric	English	Comments
Adhesive Bond Strength	30.0 MPa	4350 psi	steel collar and pin shear; ISO 10123

Thermal Properties	Metric	English	Comments
CTE, linear	90.0 µm/m-°C	50.0 µin/in-°F
Thermal Conductivity	0.190 W/m-K	1.32 BTU-in/hr-ft²-°F

Electrical Properties	Metric	English	Comments
Dielectric Strength	11.0 kV/mm	279 kV/in

Processing Properties	Metric	English	Comments
Cure Time	4.98 min @Temperature 23.0 °C	0.0830 hour @Temperature 73.4 °F	Brass, handling strength
	7.02 min @Temperature 23.0 °C	0.117 hour @Temperature 73.4 °F	Zinc, handling strength
	4.98 - 10.2 min @Temperature 23.0 °C	0.0830 - 0.170 hour @Temperature 73.4 °F	M10 steel, handling strength
	15.0 min @Temperature 23.0 °C	0.250 hour @Temperature 73.4 °F	Brass, working strength
	30.0 min @Temperature 23.0 °C	0.500 hour @Temperature 73.4 °F	Stainless steel, handling strength
	60.0 min @Temperature 23.0 °C	1.00 hour @Temperature 73.4 °F	Zinc, working strength
	120 min @Temperature 23.0 °C	2.00 hour @Temperature 73.4 °F	M10 steel, working strength
	1440 min @Temperature 23.0 °C	24.0 hour @Temperature 73.4 °F	M10 steel, full strength
	1440 min @Temperature 23.0 °C	24.0 hour @Temperature 73.4 °F	Zinc, full strength
	1440 min @Temperature 23.0 °C	24.0 hour @Temperature 73.4 °F	Stainless steel, working strength

Descriptive Properties	Value	Comments
Appearance	Green	Uncured
Maximum Gap Fill (mm)	0.2
Maximum Thread Size	M25
Strength Retention	50% at 150°C	Relative to 0°C
	80% at 100°C	Relative to 0°C
	93% at 50°C	Relative to 0°C
Torque Strength (N m)	31	M10 steel, break
	50	M10 steel, prevail
UV Fluorescence	No	Uncured