Permabond HH131 High Temperature Threadlocker
| Category | Polymer , Adhesive , Thermoset , Acrylic/Cyanoacrylate Adhesive |
| Manufacturer | Permabond |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Permabond HH131 High Temperature Threadlocker.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Permabond® HH131 is a very high temperature resistant, high strength anaerobic threadlocker and sealant. This material cures in the absence of air between tight fitting metal parts. It is used for locking bolts, nuts and screws that require permanent assembly. This material is best suited for applications requiring high temperature resistance. Features & Benefits: Vibration resistant Very high strength Excellent chemical resistance Lubricates threads for easier assembly High temperature resistance Information provided by Permabond.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | Uncured |
| Viscosity | 7500 cP @Temperature 25.0 °C |
7500 cP @Temperature 77.0 °F |
at 20 rpm vibration |
| 23000 cP @Temperature 25.0 °C |
23000 cP @Temperature 77.0 °F |
at 2 rpm vibration | |
| Storage Temperature | 5.00 - 25.0 °C | 41.0 - 77.0 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Adhesive Bond Strength | 17.0 MPa | 2470 psi | steel collar and pin shear; ISO 10123 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C | 50.0 µin/in-°F | |
| Thermal Conductivity | 0.190 W/m-K | 1.32 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 229 °C | 445 °F | |
| Minimum Service Temperature, Air | -53.9 °C | -65.0 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 11.0 kV/mm | 279 kV/in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 15.0 min @Temperature 23.0 °C |
0.250 hour @Temperature 73.4 °F |
M10 steel, handling strength |
| 30.0 min @Temperature 23.0 °C |
0.500 hour @Temperature 73.4 °F |
Zinc, handling strength | |
| 60.0 min @Temperature 23.0 °C |
1.00 hour @Temperature 73.4 °F |
Aluminum, handling strength | |
| 180 min @Temperature 23.0 °C |
3.00 hour @Temperature 73.4 °F |
Zinc, working strength | |
| 180 - 360 min @Temperature 23.0 °C |
3.00 - 6.00 hour @Temperature 73.4 °F |
M10 steel, working strength | |
| 1440 min @Temperature 23.0 °C |
24.0 hour @Temperature 73.4 °F |
M10 steel, full strength | |
| 4320 min @Temperature 23.0 °C |
72.0 hour @Temperature 73.4 °F |
Aluminum, working strength |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Red | Uncured |
| Maximum Gap Fill (mm) | 0.3 | |
| Maximum Thread Size | M56 | |
| Strength Retention | 20% at 250°C | Relative to 0°C |
| 60% at 200°C | Relative to 0°C | |
| 87% at 150°C | Relative to 0°C | |
| 93% at 100°C | Relative to 0°C | |
| 98% at 50°C | Relative to 0°C | |
| Torque Strength (N m) | 27 | M10 steel, break |
| 54 | M10 steel, prevail | |
| UV Fluorescence | No | Uncured |
Users viewing this material also viewed the following:
- MV Labs TI550 (NH4)2TiF6 Ammonium hexafluorotitanate
- Oxford Polymers 30CF 30% Carbon Fiber Reinforced Polyphenylene Sulfide
- Nilit FRIANYL A63 HS-GV10 Nylon 6.6 for injection molding, 10% glass fiber reinforced
- SABIC Innovative Plastics Lexan® 9945A PC (Asia Pacific)
- Polymer Resources NY6-GP1 General Purpose Nylon 6
- Overview of materials for Polycarbonate/Styrenic Alloy
- Firestone CR212-203-D Nylon 6, Heat Stabilized
- Lanxess Pocan® B 1505 Z 000000 PBT
- LATI Latamid 66 H2 G/30 PA 66, 30% Glass Fiber Reinforced, Heat Stabilized
- Lucite International Elvacite ® 4045 Acrylic Resin
Copyright © lookpolymers.com All Rights Reserved