Eurotec® Tecomid® NB50 NL IT PA6, impact modified, super tough, natural, extrusion grade
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade |
| Manufacturer | Eurotec |
| Trade Name | Tecomid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurotec® Tecomid® NB50 NL IT PA6, impact modified, super tough, natural, extrusion grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Eurotec®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | ISO 1183 |
| Moisture Absorption | 2.30 % @Temperature 23.0 °C |
2.30 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | ISO 527 |
| Elongation at Break | >= 200 % | >= 200 % | ISO 527 |
| Tensile Modulus | 0.250 GPa | 36.3 ksi | ISO 527 |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² @Temperature -30.0 °C |
9.52 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 223 °C | 433 °F | [10 K/min], ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
|
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 230 - 250 °C | 446 - 482 °F | |
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Throat |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | ISO 960 |
| Hold Pressure | 50.0 - 100 MPa | 7250 - 14500 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Injection Speed | Medium - Fast |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PP CIP16020FCS Polypropylene, Fast Cycle
- Polimeri Europa Edistir RCL 600 Polystyrene (discontinued **)
- Mar-Bal MB1000-10 Thermoset Polyester Composite Molding Compound
- Hexcel® HexPly® F515 Epoxy Resin, 7781 Glass Fabric
- Polyram RamSter PF340S6 PBT, 30% Glass Beads
- Cossa Polimeri ESTALENE EN 10 EC Modified Polyolefin Blend
- EMS-Grivory Grivory® HT2V-3X V0 nat 6059 PA6T/66-GF30
- DuPont™ Nomex® 411 Paper, 23 mil Nominal Thickness
- DuPont Teijin Films Teijin® Tetoron® U2 Polyester Film, 200 Gauge
- Buckeye Polymers BP RPP 3009 GKW Polypropylene, Glass Filled
Copyright © lookpolymers.com All Rights Reserved