Permabond A134 Anaerobic Retainer

Category	Polymer , Adhesive , Thermoset , Acrylic/Cyanoacrylate Adhesive
Manufacturer	Permabond
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Permabond A134 Anaerobic Retainer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Permabond® A134 is a high-strength anaerobic product designed for the permanent locking and sealing of metal parts. Its 'non-drip' formulation makes it suitable for use on larger fittings, coarse threads or for the renovation of assemblies where wide tolerances are expected due to damage or wear. A134 can extend the life of components by reducing the effects of corrosion in aggressive environments. Features & Benefits Easy to apply Thixotropic Room temperature cure Very high strength Excellent chemical resistance WRAS listed for contact with wholesome (potable) water Information provided by Permabond.

Physical Properties	Metric	English	Comments
Specific Gravity	1.10 g/cc	1.10 g/cc	Uncured
Viscosity	8000 cP @Temperature 25.0 °C	8000 cP @Temperature 77.0 °F	at 20 rpm vibration
	70000 cP @Temperature 25.0 °C	70000 cP @Temperature 77.0 °F	at 2 rpm vibration
Storage Temperature	5.00 - 25.0 °C	41.0 - 77.0 °F

Mechanical Properties	Metric	English	Comments
Adhesive Bond Strength	21.0 MPa	3050 psi	steel collar and pin shear; ISO 10123

Thermal Properties	Metric	English	Comments
CTE, linear	90.0 µm/m-°C	50.0 µin/in-°F
Thermal Conductivity	0.190 W/m-K	1.32 BTU-in/hr-ft²-°F

Electrical Properties	Metric	English	Comments
Dielectric Strength	11.0 kV/mm	279 kV/in

Processing Properties	Metric	English	Comments
Cure Time	4.98 min @Temperature 23.0 °C	0.0830 hour @Temperature 73.4 °F	Brass, handling strength
	15.0 min @Temperature 23.0 °C	0.250 hour @Temperature 73.4 °F	Zinc, handling strength
	15.0 min @Temperature 23.0 °C	0.250 hour @Temperature 73.4 °F	M10 steel, handling strength
	30.0 min @Temperature 23.0 °C	0.500 hour @Temperature 73.4 °F	Brass, working strength
	60.0 min @Temperature 23.0 °C	1.00 hour @Temperature 73.4 °F	M10 steel, working strength
	360 min @Temperature 23.0 °C	6.00 hour @Temperature 73.4 °F	Zinc, working strength
	360 min @Temperature 23.0 °C	6.00 hour @Temperature 73.4 °F	Stainless steel, handling strength
	1440 min @Temperature 23.0 °C	24.0 hour @Temperature 73.4 °F	M10 steel, full strength

Descriptive Properties	Value	Comments
Appearance	Green	Uncured
Maximum Gap Fill (mm)	0.5
Maximum Thread Size	M80
Strength Retention	50% at 150°C	Relative to 0°C
	80% at 100°C	Relative to 0°C
	95% at 50°C	Relative to 0°C
Torque Strength (N m)	25	M10 Zn plated, break
	30	M10 steel, break
	45	M10 Zn plated, prevail
	50	M10 steel, prevail
UV Fluorescence	Yes	Uncured