SABIC Innovative Plastics LNP STAT-KON JX89626 PES
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON JX89626 PES.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* JX89626 is a compound based on Polyethersulfone containing Proprietary Fillers. Added feature of this material is: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D792 |
| Density | 1.41 g/cc | 0.0509 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.490 % | 0.490 % | 50% RH, 24 hrs; ASTM D570 |
| 0.710 % | 0.710 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0080 cm/cm @Time 86400 sec |
0.0050 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 161 MPa | 23400 psi | 5 mm/min; ISO 527 |
| 163 MPa | 23600 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.1 % | 2.1 % | Type I, 5 mm/min; ASTM D638 |
| 2.2 % | 2.2 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 11.16 GPa | 1619 ksi | 1 mm/min; ISO 527 |
| 11.94 GPa | 1732 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 226 MPa | 32800 psi | ISO 178 |
| 238 MPa | 34500 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 9.67 GPa | 1400 ksi | 2 mm/min; ISO 178 |
| 10.1 GPa | 1460 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.490 J/cm | 0.918 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.95 J/cm | 11.1 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 36.0 kJ/m² | 17.1 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 47.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
26.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 38.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
21.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 219 °C | 426 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 220 °C @Thickness 3.20 mm |
428 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 214 °C @Thickness 3.20 mm |
417 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 2.0 - 5.0 ohm | 2.0 - 5.0 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Park Electrochemical Nelco® NY9233 PTFE Laminate, Woven-Glass Reinforced
- RheTech Products HP512-00 High Performance Polypropylene Copolymer, Non-UV Stabilized, Natural
- Lehmann & Voss LUVOCOM® 1105-8169 PEEK, with carbon fiber
- Huntsman Araldite GY 9613 Bisphenol A Epoxy Liquid Resin
- Isoflon PA 6G Cast Polyamide 6
- Polyram PlusTek PA880 Nylon 6.6, Impact Modified
- Akzo Nobel Trigonox® SBP Polymerization Initiator
- Cheng Yu Plastic FR200GV45 Flame Retardant Nylon 66, 45% Glass Fiber
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 60 PHR N774 (SRF) Filler
Copyright © lookpolymers.com All Rights Reserved