PTS Trilac® ABS-HS5500 High Impact ABS Resin
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | Polymer Technology & Services, LLC (PTS) |
| Trade Name | Trilac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PTS Trilac® ABS-HS5500 High Impact ABS Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D792 |
| Melt Flow | 20 g/10 min @Load 10.0 kg, Temperature 220 °C |
20 g/10 min @Load 22.0 lb, Temperature 428 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Yield | 51.7 MPa | 7500 psi | ASTM D638 |
| Flexural Yield Strength | 70.3 MPa | 10200 psi | ASTM D790 |
| Flexural Modulus | 2.34 GPa | 339 ksi | ASTM D790 |
| Izod Impact, Notched | 2.67 J/cm @Thickness 6.35 mm |
5.00 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 2.99 J/cm @Thickness 3.17 mm |
5.60 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 96.0 °C | 205 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
|
| HB @Thickness 3.17 mm |
HB @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 193 °C | 380 °F | |
| Middle Barrel Temperature | 216 °C | 420 °F | |
| Front Barrel Temperature | 232 °C | 450 °F | |
| Melt Temperature | 218 - 260 °C | 425 - 500 °F | Nozzle temp not greater than stock |
| Mold Temperature | 48.9 - 65.6 °C | 120 - 150 °F | |
| Drying Temperature | 87.8 - 93.3 °C | 190 - 200 °F | |
| Dry Time | 2 - 24 hour | 2 - 24 hour | |
| Injection Pressure | 68.9 - 82.7 MPa | 10000 - 12000 psi | |
| Back Pressure | 0.689 MPa | 100 psi | |
| Screw Speed | 50 - 60 rpm | 50 - 60 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Fill Speed | Slow to Moderate |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE A 8620 BLK
- Plenco 51045 PET, Pellet, Injection Molded, Black (discontinued **)
- Inno-Comp INNOPOL® CS 1-3810 10% Glass-Fiber-Filled Polypropylene Homopolymer
- SABIC Innovative Plastics LNP THERMOCOMP BF006 SAN (Europe-Africa-Middle East)
- SABIC Innovative Plastics NORYL PX1390 PPE+PS
- Techmer ES HiFill® PA6/6 GF60 TL10 60% Glass Filled
- Westlake Plastics Kynar® 740 PVDF Homopolymer
- Chevron Phillips MarFlex® 1017 General Purpose Coating Resin
- Fainplast Compounds GS 65/R-AS Flexible PVC, Injection Molding for Footwear
- Ascend Performance Materials Vydyne® R513H Nylon 66, 13% Glass Filled, Dry as Molded
Copyright © lookpolymers.com All Rights Reserved