PTS PCA-2010NHV Non-Bromine, Non-Chlorine, Flame Retardant UV PC/ABS Alloy
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Polymer Technology & Services, LLC (PTS) |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PTS PCA-2010NHV Non-Bromine, Non-Chlorine, Flame Retardant UV PC/ABS Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This is a non-halogenated flame retardant, UV stabilized grade. Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.004 - 0.007 cm/cm | 0.004 - 0.007 in/in | ASTM D955 |
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 260 °C |
15 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 60.0 MPa @Thickness 3.17 mm |
8700 psi @Thickness 0.125 in |
ASTM D638 |
| Elongation at Break | 50 % @Thickness 3.17 mm |
50 % @Thickness 0.125 in |
ASTM D638 |
| Flexural Yield Strength | 89.0 MPa @Thickness 3.17 mm |
12900 psi @Thickness 0.125 in |
ASTM D790 |
| Flexural Modulus | 2.57 GPa @Thickness 3.17 mm |
373 ksi @Thickness 0.125 in |
ASTM D790 |
| Izod Impact, Notched | 5.34 J/cm @Thickness 3.17 mm |
10.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL File E155285 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 232 - 266 °C | 450 - 510 °F | |
| Middle Barrel Temperature | 246 - 274 °C | 475 - 525 °F | |
| Front Barrel Temperature | 246 - 288 °C | 475 - 550 °F | |
| Nozzle Temperature | 246 - 288 °C | 475 - 550 °F | |
| Melt Temperature | 246 - 288 °C | 475 - 550 °F | |
| Mold Temperature | 57.2 - 85.0 °C | 135 - 185 °F | |
| Drying Temperature | 96.1 °C | 205 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Injection Pressure | 68.9 - 110 MPa | 10000 - 16000 psi | |
| Back Pressure | 0.172 - 0.689 MPa | 25.0 - 100 psi | |
| Screw Speed | 25 - 75 rpm | 25 - 75 rpm |
Users viewing this material also viewed the following:
- LG Chemical LUMID GP2309A(W) PA6+GF30%, General Purpose
- Techmer ES HiFill FR® PA6/6 GF30 FR BK 30% Glass Filled
- A. Schulman POLYBATCH™ Blue 4500GZ Concentrate Based in Low-Density Polyethylene
- Covestro Makrolon® 2467 Polycarbonate
- ExxonMobil Santoprene® 291-75B150 Thermoplastic Vulcanizate
- 3M FP012502 White Polyester Label Products
- Ascend Performance Materials Vydyne® 41H Nylon 66, Impact Modified, Conditioned
Copyright © lookpolymers.com All Rights Reserved