- Special Metals INCOLOY® Alloy MA 956
Special Metals INCOLOY® Alloy MA 956
| Category | Metal , Superalloy , Iron Base |
| Manufacturer | Special Metals (includes the former Inco Alloys International Inc.) |
| Trade Name | INCOLOY® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Special Metals INCOLOY® Alloy MA 956.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
An iron-chromium-aluminum alloy that is oxide dispersion strengthened and produced by mechanical alloying. Production involves high-energy milling of metal powders to create an alloy with a strengthening yttrium oxide dispersoid that remains stable to the alloy's melting point. The alloy has exceptional strength and resistance to oxidation, carburization, and hot corrosion at temperatures to over 2000°F (1100°C). Used for gas-turbine combustion chambers, advanced energy-conversion systems, and other applications involving rigorous conditions. Standard product forms are round, flats, extruded section, tube, plate, sheet, and wire.Data provided by the manufacturer, Special Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.25 g/cc | 0.262 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 650 MPa | 94300 psi | Annealed |
| 590 MPa @Temperature 300 °C |
85600 psi @Temperature 572 °F |
Annealed prior to test | |
| Tensile Strength, Yield | 550 MPa | 79800 psi | Annealed |
| 480 MPa @Temperature 300 °C |
69600 psi @Temperature 572 °F |
Annealed prior to test | |
| Elongation at Break | 9.0 % | 9.0 % | Annealed prior to test. |
| 9.0 % @Temperature 300 °C |
9.0 % @Temperature 572 °F |
Annealed prior to test. |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 11.3 µm/m-°C @Temperature 20.0 - 100 °C |
6.28 µin/in-°F @Temperature 68.0 - 212 °F |
|
| Specific Heat Capacity | 0.469 J/g-°C | 0.112 BTU/lb-°F | |
| Thermal Conductivity | 10.9 W/m-K | 75.6 BTU-in/hr-ft²-°F | |
| Melting Point | 1311 - 1400 °C | 2392 - 2550 °F | |
| Solidus | 1311 °C | 2392 °F | |
| Liquidus | 1400 °C | 2550 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | 4.5 % | 4.5 % | |
| Chromium, Cr | 20 % | 20 % | |
| Iron, Fe | 74 % | 74 % | |
| Titanium, Ti | 0.50 % | 0.50 % | |
| Y2O3 | 0.50 % | 0.50 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.000131 ohm-cm | 0.000131 ohm-cm |
Users viewing this material also viewed the following:
- Nyco NYAD® 5000 WOLLASTOCOAT® Wollastonite
- Michelman® Michem® Emulsion 21030 Anionic polyethylene emulsion
- SABIC Innovative Plastics NORYL PX6120 PPE+PS
- SABIC Innovative Plastics Valox® 553M PBT+PC (Asia Pacific)
- Saint-Gobain CHR® SG56-03(R) Anti-Static Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
- Solvay MACKAZOLINE® O-V Surfactant
- Silberline Sparkle Silvex® Premier 838-20-D
- Ineos Nova 6260 Super High Impact Polystyrene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved