SABIC Innovative Plastics NORYL PX138H PPE+HIPS (Asia Pacific)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL PX138H PPE+HIPS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Modified PPO Resin with 20% Glass Fibre Reinforced
Physical Properties Metric English Comments
Specific Gravity 1.23 g/cc
1.23 g/cc
ASTM D792
Density 1.23 g/cc
0.0444 lb/in³
ISO 1183
Moisture Absorption 0.0400 %
0.0400 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.12 %
0.12 %
ISO 62
Linear Mold Shrinkage, Flow 0.0045 - 0.0055 cm/cm

@Thickness 3.20 mm
 0.0045 - 0.0055 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 2.7 g/10 min

@Load 5.00 kg,
Temperature 280 °C
 2.7 g/10 min

@Load 11.0 lb,
Temperature 536 °F
 ASTM D1238
Melt Index of Compound 2.0 g/10 min

@Load 5.00 kg,
Temperature 280 °C
 2.0 g/10 min

@Load 11.0 lb,
Temperature 536 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 90.0 MPa
13100 psi
5 mm/min; ISO 527
100 MPa
14500 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 90.0 MPa
13100 psi
5 mm/min; ISO 527
100 MPa
14500 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 3.0 %
3.0 %
Type I, 5 mm/min; ASTM D638
3.0 %
3.0 %
5 mm/min; ISO 527
Elongation at Yield 3.0 %
3.0 %
Type I, 5 mm/min; ASTM D638
3.0 %
3.0 %
5 mm/min; ISO 527
Tensile Modulus 6.00 GPa
870 ksi
1 mm/min; ISO 527
6.50 GPa
943 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 140 MPa
20300 psi
1.3 mm/min, 50 mm span; ASTM D790
150 MPa
21800 psi
2 mm/min; ISO 178
Flexural Modulus 5.30 GPa
769 ksi
1.3 mm/min, 50 mm span; ASTM D790
5.40 GPa
783 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.900 J/cm
1.69 ft-lb/in
ASTM D256
1.00 J/cm

@Temperature -30.0 °C
 1.87 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Notched (ISO) 30.0 kJ/m²
14.3 ft-lb/in²
80*10*4; ISO 180/1A
33.0 kJ/m²

@Temperature -30.0 °C
 15.7 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 20.0 J

@Temperature 23.0 °C
 14.8 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 27.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 15.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
34.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 18.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 75.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 41.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
82.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 45.6 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 135 °C
275 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
137 °C

@Thickness 3.20 mm
 279 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Vicat Softening Point 143 °C
289 °F
Rate B/50; ASTM D1525
143 °C
289 °F
Rate B/50; ISO 306
147 °C
297 °F
Rate B/120; ISO 306