SABIC Innovative Plastics LNP THERMOCOMP PFW64 PA 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP PFW64 PA 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* PFW64 is a compound based on Nylon 6 resin containing 20% Glass Fiber, 30% Wollastonite.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.63 g/cc | 0.0589 lb/in³ | ASTM D792 |
| 1.63 g/cc | 0.0589 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.750 % | 0.750 % | 50% RH, 24 hrs; ASTM D570 |
| 0.980 % | 0.980 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.010 cm/cm @Time 86400 sec |
0.0080 - 0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 133 MPa | 19300 psi | 5 mm/min; ISO 527 |
| 135 MPa | 19600 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 |
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 11.48 GPa | 1665 ksi | 1 mm/min; ISO 527 |
| 12.3 GPa | 1780 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 169 MPa | 24500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 195 MPa | 28300 psi | ISO 178 | |
| Flexural Modulus | 9.23 GPa | 1340 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 10.62 GPa | 1540 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Unnotched | 8.07 J/cm | 15.1 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 39.0 kJ/m² | 18.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 33.7 µm/m-°C @Temperature -30.0 - 30.0 °C |
18.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 72.5 µm/m-°C @Temperature -30.0 - 30.0 °C |
40.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 216 °C @Thickness 3.20 mm |
421 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 201 °C | 394 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 203 °C @Thickness 3.20 mm |
397 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Huntsman DY 9577 Special Hardener
- SABIC Innovative Plastics LNP LUBRICOMP OL003A PPS - Branched
- SABIC Innovative Plastics ULTEM MD131A PEI
- Special Metals DURANICKEL® 301 (UNS N03301) Hot-Finished and Aged Rod and Bar
- A. Schulman LP552-01 Narrow Molecular Weight Copolymer, High-Density Polyethylene
- A. Schulman PP 1116-01 Polypropylene Molding Grade Copolymer Polypropylene
- DuPont Teijin Films Melinex® 314 Polyester Film, 200 Gauge
- Eurostar Starflam AFR450B1 PA66, Glass Fiber Reinforced, Flame Retardant, Injection Molding
- BASF Paliotan® Yellow L 1145 Color Additive
- DuPont™ Surlyn® 2601B Sodium Ionomer
Copyright © lookpolymers.com All Rights Reserved