Polymer Property : Tensile Strength, Ultimate = 60.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	60.0 MPa	8700 psi	ASTM D638
Nylene® Naxel™ A914 Polycarbonate/ABS Alloy Description: Naxel™ A914 is a Polycarbonate/ABS alloy. Information provided by Custom Resins. ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric Resources Corporation.
Tensile Strength, Ultimate	60.0 MPa	8700 psi	ASTM D638
PTS Trimid® N66-T100 Toughened Nylon 6/6 Information provided by Polymer Technology and Services, LLC (PTS).
Tensile Strength, Ultimate	60.0 MPa	8700 psi	ASTM D882
SABIC Innovative Plastics Lexan® FR60 Polycarbonate Film, Flame Retardant Lexan FR60 flame-retardant film is a clear, thin-gauge polycarbonate film with polished surfaces on both sides, and a UL94 V-0 listing to meet the stringent requirements in a wide range of electrica..
Tensile Strength, Ultimate	60.0 MPa @Temperature 60.0 °C	8700 psi @Temperature 140 °F	ISO 527
LATI LATAN 13 G/303 30% Glass Fiber Reinforced Polyoxymethylene Copolymer (POM) (discontinued **) Description: Latan series thermoplastics are polyoxymethylene copolymer (POM) products. The main applications for Latan feature good wear resistance, chemical inertness and low water absorption (gea..
Tensile Strength, Ultimate	60.0 - 74.0 MPa	8700 - 10700 psi	Average value: 68.0 MPa Grade Count:24
Overview of materials for Polycarbonate, Extruded This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Extruded". Each property range of values reported is minimum and maximum values of approp..
Tensile Strength, Ultimate	60.0 MPa	8700 psi	ISO 527
LATI LATILUB 82-01M Nylon 12 Base, 1% Molybdenum Disulfide Self Lubricating Plastic (discontinued **) Description: Latilub self-lubricating plastic materials are more and more often designed to replace metals in applications such as gears, bushings, cams, slides, etc), for which, besides their intri..
Tensile Strength, Ultimate	60.0 - 250 MPa	8700 - 36300 psi	Average value: 131 MPa Grade Count:27
Overview of materials for Nylon 12, Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, Carbon Fiber Filled". Each property range of values reported is minimum and maximum values of ..
Tensile Strength, Ultimate	60.0 - 140 MPa	8700 - 20300 psi	Average value: 110 MPa Grade Count:30
Overview of materials for Nylon 12, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. ..
Tensile Strength, Ultimate	60.0 MPa @Temperature 22.0 Â°C	8700 psi @Temperature 71.6 Â°F	25mm flat samples, compression moulded; ISO 527-4
Menzolit MenzolitÂ® SMC 0200 Unsaturated Polyester UP SMC 0200 is a general purpose SMC for a wide range of applications. Typically, it is used as housings, covers and functional components in mechanical engineering. The flammability meets the demands ..
Tensile Strength, Ultimate	60.0 MPa @Temperature 22.0 Â°C	8700 psi @Temperature 71.6 Â°F	25mm flat samples, compression moulded; ISO 527-4
Menzolit MenzolitÂ® SMC 1000 Unsaturated Polyester UP SMC 1000 is a special SMC for hydrolysis resistant applications. The glass level has been selected to combine good mouldability with good strength and stiffness properties. Typical applications are ..
Tensile Strength, Ultimate	60.0 MPa @Temperature 22.0 Â°C	8700 psi @Temperature 71.6 Â°F	25mm flat samples, compression moulded; ISO 527-4
Menzolit MenzolitÂ® SMC 0160 Unsaturated Polyester UP SMC 0160 is a general purpose SMC for applications in the field of electrical industry. Typical applications are housings, covers, wire distribution boxes and metering cabinets. The material meets ..
Tensile Strength, Ultimate	60.0 MPa @Temperature 22.0 Â°C	8700 psi @Temperature 71.6 Â°F	25mm flat samples, compression moulded; ISO 527-4
Menzolit MenzolitÂ® SMC 0290 Unsaturated Polyester UP SMC 0290 is a specially formulated SMC processable by injection moulding. The gentle production process prevents the fiber from any damage. Parts made of SMC 0290 reach higher levels of strength and..
Tensile Strength, Ultimate	60.0 MPa @Temperature 22.0 Â°C	8700 psi @Temperature 71.6 Â°F	25mm flat samples, compression moulded; ISO 527-4
Menzolit MenzolitÂ® SMC 2500 Unsaturated Polyester UP SMC 2500 is a special SMC for high voltage isolating applications. The glass level has been selected to combine good mouldability with good strength and stiffness properties. Even without a specific..
Tensile Strength, Ultimate	60.0 MPa	8700 psi	ASTM D638
LG Chemical Lupoy 3010-30 Polycarbonate Resin Description: LUPOY PC 3010-30 resin is designed for injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength.Main Character..
Tensile Strength, Ultimate	60.0 MPa	8700 psi
Saint-Gobain MicaverÂ® Glass-Mica Electrical Insulator, Compression Moldings Glass-mica compound that occupies a place between plastics and ceramics in terms of usage temperature. It can be molded and machined like plastics and has the mechanical properties (strength, hardn..
Tensile Strength, Ultimate	60.0 MPa	8700 psi	ISO 527
Solvay TechnylÂ® A 205F Nylon 66, EH0 Unreinforced polyamide 66, high fluidity, fast cycling grade, for injection molding.Technyl A 205F offers two main advantages: excellent filling qualities and UL 94 V2 under 0.4 mm. It is particula..
Tensile Strength, Ultimate	60.0 MPa	8700 psi	ASTM D638
Plenco 3509 Phenolic, Granular, Transfer Molded PLENCO 03509 is a mineral and flock filled phenolic molding compound offering excellent electrical properties, dimensional stability, and improved heat resistance. UL recognized under component file..
Tensile Strength, Ultimate	60.0 MPa	8700 psi	ISO 527-1, 2
Polyplastics Duranex® 300FP Polybutylene Terephthalate (PBT), Unfilled PBT for film, Extrusion, High Flow DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
Tensile Strength, Ultimate	60.0 MPa	8700 psi	5mm/min; ISO 527-1, 2
Polyplastics TOPAS® 6015 Cyclic Olefin Copolymer (COC) (Asia/Pacific Grade) A similar grade to 6013. However, heat deflection temperature is (HDT/B) = 150°C. This is a temperature that cannot be achieved with many other amorphous polymers.Information provided by PolyPlasti..
Tensile Strength, Ultimate	60.0 MPa	8700 psi	ASTM D882
Chengdu Polyster KLX-G11 PC Film & Sheet PC film and sheet, high transparency, both sides are polished, both sides with transparent protective films. Is printable, flame-retardant, anti-static, resists ultraviolet decay, scratch resistant,..
Tensile Strength, Ultimate	60.0 MPa @Temperature 200 °C	8700 psi @Temperature 392 °F	ISO 527-1/-2
DSM Stanyl® OCD2300 BLK PA46-GF50 50% Glass Reinforced, Heat Stabilized
Tensile Strength, Ultimate	60.0 MPa	8700 psi	5mm/min; ISO 527
BASF Ultramid® 8231G HS BK-102 14% Glass Filled PA6 (Conditioned) Ultramid 8231G HS BK-102 is a black pigmented heat stabilized, 14% glass fiber reinforced PA6 injection molding compound.The glass fiber reinforcement enhances performance such as strength, stiffnes..
Tensile Strength, Ultimate	60.0 MPa	8700 psi	ASTM D638
Chem Polymer Durlex 700 PBT, General Purpose A lubricated, general purpose PBT.Data provided by the manufacturer, Chem Polymer.
Tensile Strength, Ultimate	60.0 MPa	8700 psi	5mm/min; ISO 527
BASF Ultramid® A3HG2 10% Glass Filled PA66 (Conditioned) Ultramid A 3HG2 is a 10% glass fiber reinforced grade of nylon 6/6 for injection molding.
Tensile Strength, Ultimate	60.0 - 150 MPa @Temperature 120 - 200 °C	8700 - 21800 psi @Temperature 248 - 392 °F	Average value: 103 MPa Grade Count:7
Overview of materials for Nylon 46, Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 46, Glass Fiber Reinforced". Each property range of values reported is minimum and maximum values ..
Tensile Strength, Ultimate	60.0 MPa	8700 psi	ASTM data at 5 mm/min.
BASF Capron® 8253 Impact Modified Nylon 6 (Conditioned) (discontinued **) Capron 8253 is an unfilled type 6 graft copolymer developed for both injection molding and extrusion applications. It is also available in heat stabilized (Capron 8253 HS) and/or pigmented versions..
Tensile Strength, Ultimate	60.0 MPa	8700 psi	ASTM D882
SABIC Innovative Plastics Lexan® FR65 Polycarbonate Film, Flame Retardant Lexan FR65 flame-retardant film is a clear, thin-gauge polycarbonate film with a velvet finish on one side and a matt finish on the other, and a UL94 V-0 listing to meet the stringent requirements i..
Tensile Strength, Ultimate	60.0 - 75.0 MPa @Time 1.80e+7 - 7.20e+7 sec	8700 - 10900 psi @Time 5000 - 20000 hour	Average value: 69.4 MPa Grade Count:2
Overview of materials for Nylon 6, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 20% Glass Fiber Filled".Specific grades with glass content between 15% and 24% are included. Ea..
Tensile Strength, Ultimate	60.0 MPa	8700 psi	ATSM D638
Ashley Polymers Ashlene® P1053R Polycarbonate A high flow transparent polycarbonate with good impact properties containing UV stabilizer.Data provided by the manufacturer
Tensile Strength, Ultimate	60.0 - 150 MPa @Temperature 60.0 - 230 °C	8700 - 21800 psi @Temperature 140 - 446 °F	Average value: 100 MPa Grade Count:8
Overview of materials for Polyphthalamide (PPA), 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% are..