Solvay Specialty Polymers Radel® R-5600 Polyphenylsulfone (PPSU)

Category Polymer , Thermoplastic , Polyphenylsulfone (PPSU)
Manufacturer Solvay Specialty Polymers
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Radel® R-5600 Polyphenylsulfone (PPSU).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Radel® R-5600 is a very high melt flow grade of Radel® polyphenylsulfone (PPSU). It is especially well-suited for parts requiring long flow length with thin walls. Radel® resins offer exceptional hydrolytic stability and toughness superior to other commercially-available, high-temperature engineering resins. They also offer high deflection temperatures and outstanding resistance to environmental stress cracking. Radel® polymers are inherently flame retardant, provide excellent thermal stability and possess good electrical properties.Features: Acid Resistant; Base Resistant; Flame Retardant; Good Chemical Resistance; Good Thermal Stability; High ESCR (Stress Crack Resist.); High Heat Resistance; Hydrolytically Stable; Steam Sterilizable; Ultra High ToughnessUses: Aerospace Applications; Aircraft Applications; Food Service ApplicationsAdditional Properties: Steam Sterilization - > 1000 CyclesInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.29 g/cc
0.0466 lb/in³
ASTM D792
Water Absorption 0.37 %

@Time 86400 sec
 0.37 %

@Time 24.0 hour
 ISO 62
Water Absorption at Saturation 1.1 %
1.1 %
ASTM D570
Linear Mold Shrinkage, Flow 0.0070 cm/cm

@Thickness 3.18 mm
 0.0070 in/in

@Thickness 0.125 in
Melt Flow 34 - 40 g/10 min

@Load 5.00 kg,
Temperature 365 °C
 34 - 40 g/10 min

@Load 11.0 lb,
Temperature 689 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength 70.3 MPa

@Thickness 3.18 mm
 10200 psi

@Thickness 0.125 in
 ASTM D638
Elongation at Break 60 - 120 %

@Thickness 3.18 mm
 60 - 120 %

@Thickness 0.125 in
 ASTM D638
Elongation at Yield 7.2 %

@Thickness 3.18 mm
 7.2 %

@Thickness 0.125 in
 ASTM D638
Tensile Modulus 2.34 GPa

@Thickness 3.18 mm
 339 ksi

@Thickness 0.125 in
 ASTM D638
Flexural Strength 91.0 MPa

@Strain 5.00 %,
Thickness 3.18 mm
 13200 psi

@Strain 5.00 %,
Thickness 0.125 in
 ASTM D790
Flexural Modulus 2.34 GPa

@Thickness 3.18 mm
 339 ksi

@Thickness 0.125 in
 ASTM D790
Izod Impact, Notched 6.90 J/cm

@Thickness 3.18 mm
 12.9 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Tensile Impact Strength 399 kJ/m²

@Thickness 3.18 mm
 190 ft-lb/in²

@Thickness 0.125 in
 ASTM D1822
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 56.0 µm/m-°C

@Thickness 3.18 mm
 31.1 µin/in-°F

@Thickness 0.125 in
Deflection Temperature at 1.8 MPa (264 psi) 207 °C

@Thickness 3.20 mm
 405 °F

@Thickness 0.126 in
 Unannealed; ASTM D648
Glass Transition Temp, Tg 220 °C
428 °F
ASTM E1356
Flammability, UL94 V-0

@Thickness 0.762 mm
 V-0

@Thickness 0.0300 in
Optical Properties Metric English Comments
Refractive Index 1.672
1.672
ASTM D542
Electrical Properties Metric English Comments
Volume Resistivity 9.00e+15 ohm-cm
9.00e+15 ohm-cm
ASTM D257
Dielectric Constant 3.44

@Frequency 6.00e+7 Hz
 3.44

@Frequency 6.00e+7 Hz
 ASTM D150
Dielectric Strength 15.0 kV/mm

@Thickness 3.18 mm
 381 kV/in

@Thickness 0.125 in
 ASTM D149
>= 200 kV/mm

@Thickness 0.0254 mm
 >= 5080 kV/in

@Thickness 0.00100 in
 ASTM D149
Processing Properties Metric English Comments
Melt Temperature 360 - 391 °C
680 - 736 °F
Mold Temperature 138 - 163 °C
280 - 325 °F
Drying Temperature 149 °C
300 °F
171 °C

@Time 14400 sec
 340 °F

@Time 4.00 hour
Descriptive Properties Value Comments
Availability Asia Pacific
Europe
Latin America
North America
Color Clear Amber; Clear/Transparent; Colors
Form Pellets
Processing Technique Injection Molding
Screw Compression Ratio 2.2:1.0