Overview of materials for Polyethylene Terephthalate (PET), 50% Glass Reinforced

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 50% Glass Reinforced
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polyethylene Terephthalate (PET), 50% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), 50% Glass Reinforced". Specific grades with glass content between 45% and 54% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.44 - 1.88 g/cc
0.0520 - 0.0679 lb/in³
Average value: 1.71 g/cc Grade Count:25
Water Absorption 0.0350 - 0.620 %
0.0350 - 0.620 %
Average value: 0.196 % Grade Count:10
Moisture Absorption at Equilibrium 0.120 - 0.210 %
0.120 - 0.210 %
Average value: 0.157 % Grade Count:8
Viscosity 15000 - 300000 cP

@Temperature 270 - 315 °C
15000 - 300000 cP

@Temperature 518 - 599 °F
Average value: 133000 cP Grade Count:2
15000 - 300000 cP

@Shear Rate 1000 - 100000 1/s
15000 - 300000 cP

@Shear Rate 1000 - 100000 1/s
Average value: 133000 cP Grade Count:2
Linear Mold Shrinkage 0.00100 - 0.00600 cm/cm
0.00100 - 0.00600 in/in
Average value: 0.00280 cm/cm Grade Count:22
Linear Mold Shrinkage, Transverse 0.00500 - 0.0100 cm/cm
0.00500 - 0.0100 in/in
Average value: 0.00768 cm/cm Grade Count:11
Mechanical Properties Metric English Comments
Hardness, Rockwell M 100 - 125
100 - 125
Average value: 118 Grade Count:5
Hardness, Rockwell R 116 - 121
116 - 121
Average value: 119 Grade Count:7
Tensile Strength, Ultimate 137 - 210 MPa
19900 - 30500 psi
Average value: 177 MPa Grade Count:16
Tensile Strength, Yield 0.866 - 195 MPa
126 - 28300 psi
Average value: 138 MPa Grade Count:9
Elongation at Break 1.00 - 6.00 %
1.00 - 6.00 %
Average value: 2.36 % Grade Count:20
Modulus of Elasticity 15.5 - 19.0 GPa
2250 - 2760 ksi
Average value: 17.0 GPa Grade Count:11
Flexural Yield Strength 177 - 300 MPa
25600 - 43500 psi
Average value: 258 MPa Grade Count:15
110 - 370 MPa

@Temperature -40.0 - 120 °C
16000 - 53700 psi

@Temperature -40.0 - 248 °F
Average value: 240 MPa Grade Count:1
Flexural Modulus 9.32 - 17.0 GPa
1350 - 2470 ksi
Average value: 13.3 GPa Grade Count:18
4.69 - 4.69 GPa

@Temperature 120 - 120 °C
680 - 680 ksi

@Temperature 248 - 248 °F
Average value: 4.69 GPa Grade Count:1
Shear Modulus >= 0.122 GPa

@Temperature -50.0 - 250 °C
>= 17.7 ksi

@Temperature -58.0 - 482 °F
Average value: 1.40 GPa Grade Count:1
Izod Impact, Notched 0.694 - 1.15 J/cm
1.30 - 2.15 ft-lb/in
Average value: 0.943 J/cm Grade Count:16
Izod Impact, Unnotched 0.932 - 9.60 J/cm
1.75 - 18.0 ft-lb/in
Average value: 6.00 J/cm Grade Count:3
Izod Impact, Notched (ISO) 9.50 - 13.0 kJ/m²
4.52 - 6.19 ft-lb/in²
Average value: 10.7 kJ/m² Grade Count:5
9.00 - 9.00 kJ/m²

@Temperature -30.0 - -30.0 °C
4.28 - 4.28 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 9.00 kJ/m² Grade Count:2
Charpy Impact Unnotched 2.40 - 6.50 J/cm²
11.4 - 30.9 ft-lb/in²
Average value: 5.20 J/cm² Grade Count:7
2.10 - 6.50 J/cm²

@Temperature -30.0 - -30.0 °C
9.99 - 30.9 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 4.62 J/cm² Grade Count:6
Charpy Impact, Notched 0.900 - 1.40 J/cm²
4.28 - 6.66 ft-lb/in²
Average value: 1.11 J/cm² Grade Count:8
0.900 - 1.40 J/cm²

@Temperature -30.0 - -30.0 °C
4.28 - 6.66 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 1.08 J/cm² Grade Count:6
Thermal Properties Metric English Comments
CTE, linear 14.0 - 30.0 µm/m-°C
7.78 - 16.7 µin/in-°F
Average value: 20.3 µm/m-°C Grade Count:11
CTE, linear, Transverse to Flow 35.0 - 100 µm/m-°C
19.4 - 55.6 µin/in-°F
Average value: 68.7 µm/m-°C Grade Count:7
Melting Point 244 - 255 °C
471 - 491 °F
Average value: 250 °C Grade Count:15
Deflection Temperature at 0.46 MPa (66 psi) 226 - 255 °C
439 - 491 °F
Average value: 245 °C Grade Count:14
Deflection Temperature at 1.8 MPa (264 psi) 204 - 240 °C
400 - 464 °F
Average value: 227 °C Grade Count:22
Flammability, UL94 HB - 5VA
HB - 5VA
Grade Count:20
Oxygen Index 20.0 - 26.0 %
20.0 - 26.0 %
Average value: 22.7 % Grade Count:3
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+13 - 1.00e+16 ohm-cm
1.00e+13 - 1.00e+16 ohm-cm
Average value: 5.77e+15 ohm-cm Grade Count:12
Surface Resistance 1.00e+14 - 1.00e+15 ohm
1.00e+14 - 1.00e+15 ohm
Average value: 2.50e+14 ohm Grade Count:6
Dielectric Constant 3.40 - 5.20
3.40 - 5.20
Average value: 3.92 Grade Count:11
Dielectric Strength 17.7 - 35.0 kV/mm
450 - 889 kV/in
Average value: 23.9 kV/mm Grade Count:9
Dissipation Factor 0.00200 - 0.220
0.00200 - 0.220
Average value: 0.0226 Grade Count:9
Arc Resistance 120 - 129 sec
120 - 129 sec
Average value: 125 sec Grade Count:3
Comparative Tracking Index 175 - 400 V
175 - 400 V
Average value: 247 V Grade Count:7
Processing Properties Metric English Comments
Processing Temperature 110 - 300 °C
230 - 572 °F
Average value: 237 °C Grade Count:5
Melt Temperature 20.0 - 300 °C
68.0 - 572 °F
Average value: 262 °C Grade Count:8
Mold Temperature 80.0 - 149 °C
176 - 300 °F
Average value: 117 °C Grade Count:11
Drying Temperature 120 - 140 °C
248 - 284 °F
Average value: 128 °C Grade Count:8
Moisture Content 0.0100 - 0.0800 %
0.0100 - 0.0800 %
Average value: 0.0329 % Grade Count:7