LG Chemical LUMILOY GN1006F Injection Molding FR mPPO
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Molded |
| Manufacturer | LG Chemical |
| Trade Name | LUMILOY |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUMILOY GN1006F Injection Molding FR mPPO.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Uses include electric/electronic parts.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ASTM D792 |
| Water Absorption | 0.3 % @Time 86400 sec |
0.3 % @Time 24.0 hour |
ASTM D570 |
| Melt Flow | 5.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
5.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 41.2 MPa @Thickness 3.20 mm |
5970 psi @Thickness 0.126 in |
ASTM D638 |
| Elongation at Break | 25 % @Thickness 3.17 mm |
25 % @Thickness 0.125 in |
ASTM D638 |
| Flexural Strength | 62.8 MPa @Thickness 3.20 mm |
9110 psi @Thickness 0.126 in |
ASTM D790 |
| Flexural Modulus | 2.26 GPa @Thickness 3.20 mm |
327 ksi @Thickness 0.126 in |
ASTM D790 |
| Izod Impact, Notched | 1.18 J/cm @Thickness 3.20 mm |
2.20 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C @Thickness 3.20 mm |
171 °F @Thickness 0.126 in |
Unannealed; ASTM D648 |
| Flammability, UL94 | V-2 @Thickness 1.50 mm |
V-2 @Thickness 0.0591 in |
|
| V-2 @Thickness 3.00 mm |
V-2 @Thickness 0.118 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 210 - 240 °C | 410 - 464 °F | |
| Middle Barrel Temperature | 220 - 250 °C | 428 - 482 °F | |
| Front Barrel Temperature | 220 - 250 °C | 428 - 482 °F | |
| Nozzle Temperature | 210 - 240 °C | 410 - 464 °F | |
| Mold Temperature | 50.0 - 70.0 °C | 122 - 158 °F | |
| Drying Temperature | 55 - 70.0 °C | 130 - 158 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Moisture Content | >= 0.01 % | >= 0.01 % |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufGuard E™ XP-115DD-Zeta PE, Flame Retardant
- PolyOne Elastamax™ EG-9190 Thermoplastic Elastomer (TPE)
- PolyOne Geon™ 140 Series 140X484 Polyvinyl Chloride Homopolymer (PVC Homopolymer)
- LG Chemical LUMID GP2500A(W) PA6+GF50%, General Purpose
- Michelman® Michem® Emulsion 44730 Nonionic ethylene acrylic acid copolymer
- SABIC Innovative Plastics LNP LUBRICOMP LL004C PEEK
- Techmer ES HiFill® PES GF20 20% Glass Filled
- Teknor Apex APEX® 90-P513A-90-NT Polyvinyl Chloride+PUR
- ATI Allvac® Vasco® Greek Ascoloy Specialty Steel, Heat Treatment: 871°C (1600°F) + Age
- GEHR Plastics ECOGEHR® PA 11 Nylon 11 Dry (discontinued **)
Copyright © lookpolymers.com All Rights Reserved