Omnia Plastica PVC Polyvinylchloride

Category Polymer , Thermoplastic , Vinyl (PVC) , PVC, Extruded
Manufacturer Omnia Plastica s.p.a.
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Omnia Plastica PVC Polyvinylchloride.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
A widely used material, its application is under regulation in many countries for ecological reasons and it is often substituted by PP or other polymers. It is chosen for its chemical resistance.Features:High chemical resistance Higher stiffness compared to polyolefins Easy machinability on mechanical tools. It can be hot welded Colour: grey, ivory, redWeak Point:Compared to PP it has lower shock and temperature resistance. The high gravity reduces its cheapness.Application:Chemical: the main application of PVC is in the chemical industry, thanks to its high resistance to acids and alkali and to its rigidity. It is used for components such as valves, flanges, gears, etc. in the chemical, galvanic and petrochemical industries. Food contact: it cannot be used in contact with food. Electrical: good dielectric properties and weather resistance make it suitable for these applications. Mechanical: it is also used for mechanical components in corrosive environments. Compared to polyolefins, it has a higher tensile stress.Information provided by Omnia Plastica s.p.a. for semifinished products such as sheet, rod, and tube.
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
ISO.1183 DIN.53479
Moisture Absorption at Equilibrium 0.10 %
0.10 %
50% relative humidity
Water Absorption at Saturation 0.10 %
0.10 %
23°C
Mechanical Properties Metric English Comments
Hardness, Rockwell M 97
97
dry sample; ISO2039.2
Ball Indentation Hardness 75.0 MPa
10900 psi
ISO2039.1 DIN.53456
Tensile Strength at Break 55.0 MPa
7980 psi
ISO.527 DIN.53455
Elongation at Break 20 %
20 %
ISO.527 DIN.53455
Tensile Modulus 2.60 GPa
377 ksi
ISO.527 DIN.53455
Compressive Strength 7.00 MPa
1020 psi
1% strain over 1000 hours; ISO.899 DIN.53444
Charpy Impact Unnotched 1.50 J/cm²
7.14 ft-lb/in²
7.5 J; ISO.R179 DIN.53453
Charpy Impact, Notched 0.400 J/cm²
1.90 ft-lb/in²
ISO179/3C DIN.53453
Thermal Properties Metric English Comments
CTE, linear 80.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
44.4 µin/in-°F

@Temperature 73.4 - 140 °F
Thermal Conductivity 0.150 W/m-K
1.04 BTU-in/hr-ft²-°F
DIN.52612
Melting Point 80.0 °C
176 °F
Maximum Service Temperature, Air 60.0 °C
140 °F
Maximum operating temperature continuously for 5000 hours based on a tensile stress of 50% at 23° C.
65.0 °C
149 °F
short period, no load
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C
140 °F
ISO.75 DIN.53461
Minimum Service Temperature, Air -5.00 °C
23.0 °F
impact conditions and heavy loads not considered
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ISO.93 DIN.53482
Dielectric Constant 3.0

@Frequency 1e+6 Hz
3.0

@Frequency 1e+6 Hz
ISO.250 DIN.53483
Dielectric Strength 50.0 kV/mm
1270 kV/in
ISO.243 DIN.53481
Dissipation Factor 0.015

@Frequency 1e+6 Hz
0.015

@Frequency 1e+6 Hz
ISO.250 DIN.53483