SABIC Innovative Plastics LNP Stat-kon DE002P PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Stat-kon DE002P PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP STAT-KON* DE002P is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.23 g/cc
0.0444 lb/in³
ASTM D 792
1.23 g/cc
0.0444 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C / 50% RH; ISO 62
0.12 %

@Time 86400 sec
 0.12 %

@Time 24.0 hour
 50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.00060 - 0.0032 cm/cm

@Time 86400 sec
 0.00060 - 0.0032 in/in

@Time 24.0 hour
 ISO 294
0.0010 - 0.0030 cm/cm

@Time 86400 sec
 0.0010 - 0.0030 in/in

@Time 24.0 hour
 ASTM D 955
Linear Mold Shrinkage, Transverse 0.0020 - 0.0040 cm/cm

@Time 86400 sec
 0.0020 - 0.0040 in/in

@Time 24.0 hour
 ASTM D 955
0.0029 - 0.0043 cm/cm

@Time 86400 sec
 0.0029 - 0.0043 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 115 MPa
16700 psi
ASTM D 638
118 MPa
17100 psi
ISO 527
Elongation at Break 2.4 %
2.4 %
ASTM D 638
2.5 %
2.5 %
ISO 527
Tensile Modulus 8.50 GPa
1230 ksi
1 mm/min; ISO 527
8.68 GPa
1260 ksi
50 mm/min; ASTM D 638
Flexural Strength 185 MPa
26800 psi
ASTM D 790
189 MPa
27400 psi
ISO 178
Flexural Modulus 7.37 GPa
1070 ksi
ASTM D 790
8.50 GPa
1230 ksi
ISO 178
Izod Impact, Notched 0.640 J/cm

@Temperature 23.0 °C
 1.20 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 4.91 J/cm

@Temperature 23.0 °C
 9.20 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 7.00 kJ/m²

@Temperature 23.0 °C
 3.33 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 34.0 kJ/m²

@Temperature 23.0 °C
 16.2 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 4.00 J
2.95 ft-lb
Multiaxial Impact; ISO 6603
14.0 J

@Temperature 23.0 °C
 10.3 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Energy @ peak; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 18.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 10.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
18.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 10.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 38.3 µm/m-°C

@Temperature -40.0 - 40.0 °C
 21.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
38.3 µm/m-°C

@Temperature -40.0 - 40.0 °C
 21.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 143 °C
289 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
143 °C

@Thickness 3.20 mm
 289 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 139 °C
282 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
140 °C

@Thickness 3.20 mm
 284 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Flammability, UL94 V-2

@Thickness 1.50 mm
 V-2

@Thickness 0.0591 in
 UL 94 by SABIC-IP
Electrical Properties Metric English Comments
Surface Resistance 100 - 1.00e+6 ohm
100 - 1.00e+6 ohm
ASTM D 257