Sibur VO Compound VNP Polyvinyl Chloride (PVC)

Category	Polymer , Thermoplastic , Vinyl (PVC) , PVC, Molded
Manufacturer	Sibur
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Sibur VO Compound VNP Polyvinyl Chloride (PVC).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Shall correspond to control sample, approved in accordance with the established procedure. Pores, which can be seen by eyes, are not allowed. Plastic shall no burn at stop of worm extruder for a period of 20 minutes. For production of internal sheaths for wires and cables by extrusion method. Use of VO material results in decrease of economic expenses during production of cable products. Specific peculiarity of this plastic is absence of adhesion to materials of insulation and sheath.

Physical Properties	Metric	English	Comments
Density	1.60 - 2.50 g/cc	0.0578 - 0.0903 lb/inÂ³
Collected Volatile Condensable Material	<= 3.0 %	<= 3.0 %	Loss in mass at 160Â°C during 6 hours

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	4.00 - 10.0 MPa	580 - 1450 psi
Elongation at Break	>= 150 %	>= 150 %

Thermal Properties	Metric	English	Comments
Brittleness Temperature	<= -15.0 Â°C	<= 5.00 Â°F
Flammability Test	<= 15	<= 15	In seconds, method A

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+10 ohm-cm @Temperature 20.0 Â°C	>= 1.00e+10 ohm-cm @Temperature 68.0 Â°F

Descriptive Properties	Value	Comments
Color	Non-colored
Elongation Retained After Ageing	80%	Aged for 7 days at 100Â±2Â°C