- Nilit RECONYL B GV30 Recycled nylon 6 for injection molding, 30% glass fiber reinforced
Nilit RECONYL B GV30 Recycled nylon 6 for injection molding, 30% glass fiber reinforced
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit RECONYL B GV30 Recycled nylon 6 for injection molding, 30% glass fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Recycled nylon 6 for injection molding (available only in black).Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Water Absorption | 1.3 - 2.3 % | 1.3 - 2.3 % | ISO 62 |
| Water Absorption at Saturation | 6.0 - 7.0 % | 6.0 - 7.0 % | ISO 62 |
| Linear Mold Shrinkage | 0.0060 - 0.017 cm/cm | 0.0060 - 0.017 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 160 MPa | 23200 psi | ISO 2039-1 |
| Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 8.30 GPa | 1200 ksi | ISO 527 |
| Flexural Modulus | 7.80 GPa | 1130 ksi | ISO 178 |
| Charpy Impact Unnotched | 2.70 J/cm² | 12.8 ft-lb/in² | DIN 53453 |
| 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179/1eU | |
| 2.30 J/cm² @Temperature -40.0 °C |
10.9 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| 3.00 J/cm² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | DIN 53453 |
| 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179/1eA | |
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 105 °C | 221 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics NORYL WCA871A PPE (Asia Pacific)
- SABIC Innovative Plastics NORYL WCD861A PPE-TPE
- Silon Taborex TA 1134 HD Chemically-Crosslinkable HDPE Compound
- Polyram RamOfin PPH300G6 Polypropylene, 30% Glass Fiber
- Elastocon TPE Technologies Elastocon® 2870 Thermoplastic Elastomer
- DuPont™ Bynel® 50E806 Anhydride Modified Polypropylene
- BASF Ultramid® S3WG7 Balance 35% Glass Filled PA 610 (Conditioned)
- ATI Allegheny Ludlum AL 409 Cb™ Brazeable Ferritic Stainless Steel, 43.6% Cold Work
Copyright © lookpolymers.com All Rights Reserved