Nilit RECONYL B F Recycled nylon 6 for injection molding

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer Nilit (formerly Frisetta Polymer)
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Nilit RECONYL B F Recycled nylon 6 for injection molding.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Recycled nylon 6 for injection molding, highly crystallized (available only in black).Information provided by Frisetta Polymer, which merged into Nilit Plastics
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ISO 1183
Water Absorption 2.2 - 3.2 %
2.2 - 3.2 %
ISO 62
Water Absorption at Saturation 8.0 - 9.0 %
8.0 - 9.0 %
ISO 62
Linear Mold Shrinkage 0.015 - 0.025 cm/cm
0.015 - 0.025 in/in
FRISETTA Test Method
Mechanical Properties Metric English Comments
Ball Indentation Hardness 130 MPa
18900 psi
ISO 2039-1
Tensile Strength at Break 75.0 MPa
10900 psi
ISO 527
Elongation at Break 45 %
45 %
ISO 527
Tensile Modulus 2.70 GPa
392 ksi
ISO 527
Flexural Strength 90.0 MPa
13100 psi
ISO 178
Flexural Modulus 2.40 GPa
348 ksi
ISO 178
Charpy Impact Unnotched NB
NB
DIN 53453
NB

@Temperature -40.0 °C
 NB

@Temperature -40.0 °F
 DIN 53453
Charpy Impact, Notched 0.400 J/cm²
1.90 ft-lb/in²
DIN 53453
Thermal Properties Metric English Comments
Melting Point 221 °C
430 °F
ISO 3146 DSC
Maximum Service Temperature, Air 80.0 °C
176 °F
Continuous; FRISETTA Test Method
Deflection Temperature at 0.46 MPa (66 psi) 160 °C
320 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C
149 °F
ISO 75