SABIC Innovative Plastics LNP THERMOCOMP EF006 PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP EF006 PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* EF006 is a compound based on Polyetherimide resin containing 30% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in³ | ISO 1183 |
| 1.528 g/cc | 0.05520 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.150 % | 0.150 % | 50% RH, 24 hrs; ASTM D570 |
| 0.210 % | 0.210 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0023 cm/cm @Time 86400 sec |
0.0023 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0049 cm/cm @Time 86400 sec |
0.0049 in/in @Time 24.0 hour |
ISO 294 |
| 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 177 MPa | 25700 psi | ISO 527 |
| 188 MPa | 27300 psi | ASTM D638 | |
| Elongation at Break | 2.2 % | 2.2 % | ISO 527 |
| 2.4 % | 2.4 % | ASTM D638 | |
| Tensile Modulus | 10.38 GPa | 1505 ksi | 1 mm/min; ISO 527 |
| 11.44 GPa | 1659 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 263 MPa | 38100 psi | ISO 178 |
| 270 MPa | 39200 psi | ASTM D790 | |
| Flexural Modulus | 11.37 GPa | 1649 ksi | ASTM D790 |
| 11.51 GPa | 1669 ksi | ISO 178 | |
| Izod Impact, Notched | 1.06 J/cm | 1.99 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.58 J/cm | 14.2 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 48.0 kJ/m² | 22.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 12.0 J | 8.85 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.55 | 0.55 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.50 | 0.50 | ASTM D3702 Modified |
| K (wear) Factor | 262 x 10-8 mm³/N-M | 130 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 41.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 41.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 30.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 30.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 203 °C @Thickness 3.20 mm |
397 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Multibase Nylex™ 2185 CR Polyamide + PP
- Nye Lubricants 188B (SO) Synthetic Oil
- SABIC Innovative Plastics Cycoloy® RCY6214 PC+ABS (Asia Pacific)
- Parker Chomerics Tecknit® 72-08116 Silver-Filled Epoxy System
- PolyOne Dynaflex™ G7960-1 NSFG Thermoplastic Elastomer (TPE)
- Chlorosulfonated Polyethylene Rubber (CM, CSM)
- SABIC Innovative Plastics NORYL SE1GFN3 PPE+HIPS (Europe-Africa-Middle East)
- A. Schulman COMTUF® 5011 10% Glass Fiber Reinforced Polycarbonate