- Nilit RECONYL A KV30 Recycled nylon 6.6 for injection molding, 30% glass ball reinforced
Nilit RECONYL A KV30 Recycled nylon 6.6 for injection molding, 30% glass ball reinforced
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit RECONYL A KV30 Recycled nylon 6.6 for injection molding, 30% glass ball reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Recycled nylon 6.6 for injection molding (available only in black).Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Water Absorption | 1.4 - 2.4 % | 1.4 - 2.4 % | ISO 62 |
| Water Absorption at Saturation | 5.5 - 6.5 % | 5.5 - 6.5 % | ISO 62 |
| Linear Mold Shrinkage | 0.0090 - 0.015 cm/cm | 0.0090 - 0.015 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 170 MPa | 24700 psi | ISO 2039-1 |
| Tensile Strength at Break | 80.0 MPa | 11600 psi | ISO 527 |
| Elongation at Break | 7.0 % | 7.0 % | ISO 527 |
| Tensile Modulus | 4.00 GPa | 580 ksi | ISO 527 |
| Flexural Strength | 110 MPa | 16000 psi | ISO 178 |
| Flexural Modulus | 3.70 GPa | 537 ksi | ISO 178 |
| Charpy Impact Unnotched | 1.80 J/cm² | 8.57 ft-lb/in² | DIN 53453 |
| 1.30 J/cm² @Temperature -40.0 °C |
6.19 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75 |
Users viewing this material also viewed the following:
- PSM Industries Pacific Sintered Metals High Carbon Copper Steel FCC-200-P Powdered Metal
- Minelco Mulcoa 60
- Schwartz Technical Plastics LAMIGAMID® 310 Cast Polyamide 6, Dry
- Borealis Daplen™ FS65T20 Polypropylene Compound 20% Mineral Filled, Detergent Resistant
- A. Schulman POLYBATCH™ MAS-25 Concentrate Based In LDPE
- ExxonMobil Light Mobil DTE Oil Named Series
- Arlon 99202R008 0.008" (0.203 mm) Cured Silicone Rubber with PTFE Coated Fiberglass Carrier
- BASF Capron® B73ZP Nylon 6 (DAM) (discontinued **)
- Phillips 66 COPYLENE® CM015G Polypropylene Impact Copolymer
- DuPont Performance Polymers Crastin® S610SF NC010 PBT (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved