E-Polymers SEPAZ® K130IM 30% Glass Fiber Reinforced Impact Modified PPS Resin
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 30% Glass Fiber Filler |
| Manufacturer | E-Polymers Co. Ltd. |
| Trade Name | SEPAZ® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | E-Polymers SEPAZ® K130IM 30% Glass Fiber Reinforced Impact Modified PPS Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyphenylene Sulfide Resin: High-performance engineering plastic SEPAZ PPS boasts excellent high-temperature resistance, flame retardancy and chemical resistance, physical strength, and its fluidity leads to good dimensional precision. SEPAZ PPS applications: switches, connectors and other electronic and electric components, alternators and other automobile components, and office equipment components including chassis parts and housings.Information Provided by E-Polymers Co., Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.48 g/cc | 1.48 g/cc | ASTM D792 |
| Water Absorption | 0.020 % @Time 86400 sec |
0.020 % @Time 24.0 hour |
|
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 142.2 MPa | 20630 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 235.44 MPa | 34148 psi | ASTM D790 |
| Flexural Modulus | 9.0252 GPa | 1309.0 ksi | ASTM D790 |
| Izod Impact, Notched | 1.37 J/cm | 2.57 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dissipation Factor | 0.0020 @Frequency 1.00e+6 Hz |
0.0020 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 300 - 330 °C | 572 - 626 °F | |
| Mold Temperature | 130 - 160 °C | 266 - 320 °F | |
| Drying Temperature | 140 °C | 284 °F | |
| Dry Time | 6 hour | 6 hour |
Users viewing this material also viewed the following:
- ACC QSil 30 QSI Quantum Silicones 50 Durometer Condensation Cure for Potting (discontinued **)
- LG Chemical AF-348 ABS, Flame Retardant, Heat Resistant, Weather Resistant
- LG Chemical Lupox® SG3250M PBT+PET+MF25%
- Grupo Repol Dinalon® B1S25 PA6 Unreinforced
- H.C. Starck Amperit® 140.067 Tungsten (W)
- Styrolution Luran® S 757 G ASA
- Zell-Metall Engineering Plastics Zellamid 1200 G at 50% RH
- Hexcel® Fibrelam® Grade 1-4/2 Panels for Aircraft Flooring
- DuPont™ Elvaloy® AC 12024S Ethylene Methyl Acrylate
- BASF Ultramid® 8281 HS GP PA6 (Dry)
Copyright © lookpolymers.com All Rights Reserved