Nilit Polynil® N66-P50N Lubed Nylon 6/6
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced, Flame Retardant |
| Manufacturer | Nilit |
| Trade Name | Polynil® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit Polynil® N66-P50N Lubed Nylon 6/6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by US distributor Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Water Absorption | 1.3 % | 1.3 % | 24 hours at 73°F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 123 | 123 | ASTM D785 |
| Tensile Strength, Yield | 89.6 MPa @Thickness 3.17 mm |
13000 psi @Thickness 0.125 in |
|
| Elongation at Break | 28 % @Thickness 3.17 mm |
28 % @Thickness 0.125 in |
|
| Flexural Yield Strength | 135.1 MPa @Thickness 3.17 mm |
19590 psi @Thickness 0.125 in |
|
| Flexural Modulus | 3.17 GPa @Thickness 3.17 mm |
460 ksi @Thickness 0.125 in |
|
| Izod Impact, Notched | 0.370 J/cm @Thickness 3.17 mm |
0.693 ft-lb/in @Thickness 0.125 in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 257 °C | 495 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 231 °C | 448 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ASTM D648 |
| Flammability, UL94 | V-2 @Thickness 1.59 mm |
V-2 @Thickness 0.0625 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 254 °C | 490 °F | |
| Middle Barrel Temperature | 268 °C | 515 °F | |
| Front Barrel Temperature | 285 °C | 545 °F | |
| Nozzle Temperature | 266 - 282 °C | 510 - 540 °F | |
| Melt Temperature | 271 - 293 °C | 520 - 560 °F | |
| Mold Temperature | 26.7 - 93.3 °C | 80.0 - 200 °F | |
| Drying Temperature | 71.1 °C | 160 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 68.9 MPa | 10000 psi | |
| Back Pressure | 0.0689 - 0.689 MPa | 10.0 - 100 psi | |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm |
Users viewing this material also viewed the following:
- KKPC KOSYN SOL 5990 Solution Styrene Butadiene Rubber (S-SBR)
- MRC Polymers NAXELLâ„¢ PC110VL Polycarbonate, Very Low MFR
- Shinil Chemical SHINNANO PA-66 Polymer Nanocomposite CHC
- Samsung Cheil Industries Infino® TK-4046H PPA, Glass Filled
- A. Schulman POLYBATCH™ ABPP-05 Antiblock Concentrate
- Ecomass® 4703ZD90 Tungsten Filled Polyurethane
- DuPont Performance Polymers Zytel® 70G13L NC010 Nylon 66 (Unverified Data**)
- Dow VORANATE™ T-80 toluene diisocyanate (TDI)
- Austin Novel Materials Texalan® 782A PCL TPU
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 40 PHR N330 (HAF) Filler
Copyright © lookpolymers.com All Rights Reserved