- ExxonMobil Escorene® LD 767.MJ Blown Film Resin (discontinued **)
ExxonMobil Escorene® LD 767.MJ Blown Film Resin (discontinued **)
| Category | Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Escorene® LD 767.MJ Blown Film Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Escorene Ultra LD 767.MJ is a low gel 29.5% vinyl acetate copolymer designed for film and compounding applications.Information provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in³ | ExxonMobil Method |
| Vinyl Acetate Content | 29.5 % | 29.5 % | ExxonMobil Method |
| Melt Flow | 3.1 g/10 min | 3.1 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 460 % | 460 % | ASTM D882 |
| Film Elongation at Break, TD | 720 % | 720 % | ASTM D882 |
| Elmendorf Tear Strength, MD | 0.787 g/micron | 20.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 8.86 g/micron | 225 g/mil | ASTM D1922 |
| Dart Drop | 5.51 g/micron | 140 g/mil | ASTM D1709 |
| Film Tensile Strength at Break, MD | 32.0 MPa | 4640 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 37.0 MPa | 5370 psi | ASTM D882 |
| 1% Secant Modulus, MD | 24.1 MPa | 3500 psi | ASTM D882 |
| 1% Secant Modulus, TD | 24.8 MPa | 3600 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 71.1 °C | 160 °F | Peak Melting Temperature; ExxonMobil Method |
| Vicat Softening Point | 46.1 °C | 115 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 3.9 % | 3.9 % | ASTM D1003 |
| Gloss | 74 % | 74 % | 45°; ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Thermal Stabilizer |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® DMX1132 PC Copolymer (Asia Pacific)
- H.C. Starck Amperit® 553.074 Tungsten Carbide-Cobalt-Chromium 86-10-4 (WC-Co-Cr)
- A. Schulman PP 3479-01 Polypropylene Random Copolymer
- A. Schulman POLYBATCH™ CE-505-E Concentrate Based In Polyethylene
- Dow DOWLEX™ IP-41 High Density Polyethylene
- 3M 7660-S Cold Shrink Silicone Rubber Termination Kits QT-III
- AK Steel TRAN-COR® H-0 CARLITE® Grain Oriented Electrical Steel
- AKG Polymers Vision PP PPH BL3004 Polypropylene Homopolymer Compound
- ExxonMobil EXXPRO™ 3433 Medium Cure Activity Grade
Copyright © lookpolymers.com All Rights Reserved