Nilit FRIANYL B63 SI20 Nylon 6 for injection molding
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL B63 SI20 Nylon 6 for injection molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6 for injection molding, ionomer impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ISO 1183 |
| Water Absorption | 2.5 - 3.0 % | 2.5 - 3.0 % | ISO 62 |
| Water Absorption at Saturation | 8.0 - 9.0 % | 8.0 - 9.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.012 - 0.020 cm/cm | 0.012 - 0.020 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 93.0 MPa | 13500 psi | ISO 2039-1 |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO 527 |
| Elongation at Break | 33 % | 33 % | ISO 527 |
| Tensile Modulus | 2.30 GPa | 334 ksi | ISO 527 |
| Flexural Strength | 60.0 MPa | 8700 psi | ISO 178 |
| Flexural Modulus | 2.10 GPa | 305 ksi | ISO 178 |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| NB | NB | DIN 53453 | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eU | |
| NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 3.50 J/cm² | 16.7 ft-lb/in² | DIN 53453 |
| 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 450 V | 450 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- Ineos Nova S-4200 Medium Impact Compact Polystyrene (discontinued **)
- Chevron Phillips HiD® 9330 HDPE Natural Pipe Resin (discontinued **)
- Mitsubishi Iupilon® E2000R 5 MFI Polycarbonate With Release
- Lushan AR-10 Nylon Toughener/PA Impact Modifier
- Struktol TR 016 Processing Additive
- Solvay ALKAMULS® EL 620 LI E Surfactant
- Wieland 1408 Wilaform Gold
- ExxonMobil Santoprene® 121-80B230 Thermoplastic Elastomer
- Arkema Group LOTRYL® 37 EH 550 Copolymer Ethylene - Acrylic Ester
Copyright © lookpolymers.com All Rights Reserved