Techmer ES Luriblend® PSU GF20 TL5 20% Glass Filled
| Category | Polymer , Thermoplastic , Polysulfone (PSU) , Polysulfone, 20% Glass Fiber Reinforced |
| Manufacturer | Techmer ES |
| Trade Name | Luriblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Luriblend® PSU GF20 TL5 20% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 20% Filler by WeightAdditive: PTFE LubricantFeatures: LubricatedInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ASTM D792 |
| Water Absorption | 0.21 % @Time 86400 sec |
0.21 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 3.17 mm |
0.0020 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 123 | 123 | ASTM D785 |
| Tensile Strength, Yield | 97.9 MPa | 14200 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 138 MPa | 20000 psi | ASTM D790 |
| Flexural Modulus | 5.86 GPa | 850 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm @Thickness 3.17 mm |
1.20 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.6 µm/m-°C | 17.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 182 °C | 360 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 16.9 kV/mm | 430 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Qualchem Danamid AFCF-30 Polyamide 66, 30% Carbon Fiber
- BASF Capron® 8202C HS Nylon 6 (Conditioned) (discontinued **)
- Kinlead PG12 Bag Grade BOPP Plain Film (thickness: 50 µm)
- Meilian Chemical PE42095 YELLOW MASTERBATCH
- Samsung Cheil Industries Starex® SD-0150AT ABS, Unreinforced
- DSM Arnite® TV6 241 T Impact Modified PBT-20% Glass Reinforced (European Grade)
- Ashley Polymers Ashlene® 830L-33G Nylon 6, 33% Glass Reinforced
- Solvay RHODAPHOSE® TRIPHENYL PHOSPHINE Phosphorus Derivative
Copyright © lookpolymers.com All Rights Reserved