Topas Advanced Polymers TOPAS® 6013F-04 Cyclic Olefin Copolymer (COC)

Category	Polymer , Thermoplastic , Cyclo Olefin Polymer
Manufacturer	Topas Advanced Polymers
Trade Name	TOPAS®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Topas Advanced Polymers TOPAS® 6013F-04 Cyclic Olefin Copolymer (COC).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

TOPAS® 6013F-04 is a high temperature, general purpose film extrusion grade. It is a high clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and healthcare applications. It is used in monolayer and blended cast applications, and in coextrusion and blends in both cast and blown processes, for a wide variety of film and sheet products requiring excellent optics in applications such as heat resistant blister, hot fill, and easy tear packaging. Key applications and attributes: Pharmaceutical blisters: Clarity, forming, barrier, purity, halogen-free Decorative film and sheet: Gloss, hardness, chemical resistance, forming Food packaging: Hot-fill, easy or linear tear, purity Healthcare and food: Broad regulatory approval Information provided by TOPAS Advanced Polymers

Physical Properties	Metric	English	Comments
Oxygen Permeability	1120 cm³ mil/(m² day atm)	72.26 cm³ mil/(100 in² day atm)
Water Vapor Permeability	6.20 g mil/ (m² day)	0.400 g mil/ (100 in² day)
Density	1.02 g/cc	0.0368 lb/in³	ISO 1183
Water Absorption at Saturation	0.010 % @Temperature 23.0 °C	0.010 % @Temperature 73.4 °F	ISO 62
Water Vapor Transmission	0.000130 g/m²/day @Temperature 38.0 °C	0.00000837 g/100 in²/day @Temperature 100 °F	90% RH; ISO 15106-3
Oxygen Transmission	28.0 cc-mm/m²-24hr-atm @Temperature 23.0 °C	71.1 cc-mil/100 in²-24hr-atm @Temperature 73.4 °F	50% RH; ASTM D3985
Thickness	70.0 microns	2.76 mil	Film
Melt Flow	0.92 g/10 min @Load 2.16 kg, Temperature 230 °C	0.92 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	2.4 %	2.4 %	ISO 527-3
Film Elongation at Break, TD	2.2 %	2.2 %	ISO 527-3
Tensile Modulus	2.25 GPa	326 ksi	Film, TD; ISO 527-3
	2.40 GPa	348 ksi	Film, MD; ISO 527-3
Elmendorf Tear Strength MD	9.0 g	9.0 g	ISO 6383-2
Elmendorf Tear Strength TD	9.0 g	9.0 g	ISO 6383-2
Dart Drop Test	<= 36.0 g	<= 0.0794 lb	F50; ISO 7765-1
Film Tensile Strength at Break, MD	55.0 MPa	7980 psi	ISO 527-3
Film Tensile Strength at Break, TD	45.0 MPa	6530 psi	ISO 527-3

Thermal Properties	Metric	English	Comments
Glass Transition Temp, Tg	138 °C	280 °F	10°C/min; ISO 11357-1,-2,-3

Optical Properties	Metric	English	Comments
Haze	<= 1.0 %	<= 1.0 %	Film; ISO 14782
Gloss	>= 100 %	>= 100 %	60°, Film; ISO 2813

Descriptive Properties	Value	Comments
Type of film extrusion	Cast	Test specimen