Nilit FRIANYL B63 S20 Nylon 6 for injection molding
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL B63 S20 Nylon 6 for injection molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6 for injection molding, impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ISO 1183 |
| Water Absorption | 2.0 - 3.0 % | 2.0 - 3.0 % | ISO 62 |
| Water Absorption at Saturation | 8.0 - 9.0 % | 8.0 - 9.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.012 - 0.022 cm/cm | 0.012 - 0.022 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 100 MPa | 14500 psi | ISO 2039-1 |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO 527 |
| Elongation at Break | 33 % | 33 % | ISO 527 |
| Tensile Modulus | 2.10 GPa | 305 ksi | ISO 527 |
| Flexural Strength | 30.0 MPa | 4350 psi | ISO 178 |
| Flexural Modulus | 1.70 GPa | 247 ksi | ISO 178 |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| NB | NB | DIN 53453 | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eU | |
| NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 2.00 J/cm² | 9.52 ft-lb/in² | DIN 53453 |
| 2.30 J/cm² | 10.9 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 500 V | 500 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- MV Labs CU200 Cu2Br2 Copper(I) bromide
- Niagara LaSalle 1117 Cold Finished Steel Bar
- PolyOne Edgetek® PS-15GF-25MN/000 Polybutylene Terephthalate (PBT), Glass/Mineral Filled (discontinued **)<
- Momentive Performance Materials HCT-30 Titanium Diboride (TiB2) Powder
- Stir SpA T 2199 A (PVC)
- Techmer ES Luriblend® HIPS TL10 BK
- Silberline Stamford "O" Standard Series
- Westlake EMAC® SP2268 24% Ethylene-Methyl Acrylate Copolymer
- Eurostar Staramide RF007ESS PA66/6, 35% Glass Filled, Injection Molded
- ExxonMobil Escorene® UL-7840C EVA Copolymer, Adhesive and Sealant Grade (discontinued **)
Copyright © lookpolymers.com All Rights Reserved