- Nilit FRIANYL B63 MG30 Nylon 6 for injection molding, 30% mineral filled
Nilit FRIANYL B63 MG30 Nylon 6 for injection molding, 30% mineral filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Mineral Filled |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL B63 MG30 Nylon 6 for injection molding, 30% mineral filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Water Absorption | 1.5 - 3.0 % | 1.5 - 3.0 % | ISO 62 |
| Water Absorption at Saturation | 6.5 - 7.5 % | 6.5 - 7.5 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0050 - 0.015 cm/cm | 0.0050 - 0.015 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 148 MPa | 21500 psi | ISO 2039-1 |
| Tensile Strength at Break | 76.0 MPa | 11000 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | Flexural; ISO 178 |
| 4.0 % | 4.0 % | ISO 527 | |
| Tensile Modulus | 5.90 GPa | 856 ksi | ISO 527 |
| Flexural Strength | 67.0 MPa | 9720 psi | ISO 178 |
| Charpy Impact Unnotched | 3.30 J/cm² | 15.7 ft-lb/in² | DIN 53453 |
| 3.50 J/cm² @Temperature -40.0 °C |
16.7 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 450 V | 450 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- Zircar Zirconia HfF-15 Hafnia Knit Textile Insulation
- LyondellBasell Petrothene® GA601033 Linear Low Density Polyethylene
- Kingfa JH950-602 Low-temperature Resistant & Flame Retardant PC/ABS Alloy
- LyondellBasell Hostacomâ„¢ BC142/1AC Polypropylene Copolymer
- Teknor Apex Monprene® MP-1823 AS Thermoplastic Elastomer
- Unifrax Fiberfrax® Roll Board Ceramic Fiber Paper
- Elgiloy® Co-Cr-Ni Alloy, Wire, 20% Cold Reduction, Heat Treated
- Covestro Makrolon® 2652 Polycarbonate
- Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 45% Cold Reduction + Aged 538°C (1000°F)/4hr/AC
- Asahi Glass Fluon® PB2515 15% Carbon Fiber, PTFE Filled Compound
Copyright © lookpolymers.com All Rights Reserved