- Dow Nordel® IP 5565 General Purpose Molding
Dow Nordel® IP 5565 General Purpose Molding
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Dow Chemical |
| Trade Name | Nordel® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow Nordel® IP 5565 General Purpose Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FormulationNordel® IP 5565
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 74 @Temperature 100 °C |
74 @Temperature 212 °F |
ML 1 + 4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 69 | 69 | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tensile Strength, Ultimate | 9.50 MPa | 1380 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Elongation at Break | 383 % | 383 % | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 50% Modulus | 0.00190 GPa | 0.276 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 100% Modulus | 0.00350 GPa | 0.508 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 200% Modulus | 0.00620 GPa | 0.899 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 300% Modulus | 0.00790 GPa | 1.15 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tear Strength | 30.8 kN/m | 176 pli | Die C, Vulcanizate, Press cured, TC95 +3min at 160°C |
| Compression Set | 65 % @Temperature 125 °C |
65 % @Temperature 257 °F |
Pellets cured MDR t'95 + 15 min, 70 hr; Method B |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | -40.0 °C | -40.0 °F | Temperature Retraction, TR-10 |
Users viewing this material also viewed the following:
- Rogers Corporation Bisco™ HT-1500 Solid Silicone Rubber
- Nanocyl PLASTICYL™ PP2001 Polypropylene with 1 wt% Multi-Wall Carbon Nanotubes
- Pau Tai Unistab BT-53C Organotin Stabilizer Butyl/Octyl Carboxylate Tin
- Glastic Laminates/Shapes 1603-2A Fiberglass-Reinforced Polyester Standoff Insulator
- Michelman® Michem® Emulsion 28640 Cationic polypropylene emulsion
- SABIC Innovative Plastics NORYL GTX GTX8720 PPE+PA (Asia Pacific)
- EMS-Griltech Griltex® 11A Copolyamide Hotmelt Adhesive (Technical Applications)
- 3M FM05540K MC Polyester Label Products
- Ascend Performance Materials Vydyne® R533H NAT Nylon 66, 33% Glass Reinforced, Conditioned
Copyright © lookpolymers.com All Rights Reserved