Nilit FRIANYL B63 D Nylon 6., std. viscosity for injection molding
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL B63 D Nylon 6., std. viscosity for injection molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6., std. viscosity for injection molding, permanently flexible, developed for dowels.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | ISO 1183 |
| Water Absorption | 2.2 - 3.2 % | 2.2 - 3.2 % | ISO 62 |
| Water Absorption at Saturation | 8.0 - 9.0 % | 8.0 - 9.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.016 - 0.024 cm/cm | 0.016 - 0.024 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 130 MPa | 18900 psi | ISO 2039-1 |
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527 |
| Elongation at Break | 25 % | 25 % | ISO 527 |
| Tensile Modulus | 2.80 GPa | 406 ksi | ISO 527 |
| Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | ISO 178 |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| NB | NB | DIN 53453 | |
| NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179/1eA |
| 0.800 J/cm² | 3.81 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 600 V | 600 V | CTI 100; IEC 112 |
| 600 V | 600 V | CTI-M 100; IEC 112 |
Users viewing this material also viewed the following:
- RheTech Products M12P100-01 12% Mica Reinforced Polypropylene, Black
- Polymax® Maxelast® P3897M TPE, PP Overmold or Standalone use
- Lehmann & Voss LUVOCOM® 1-0935 Polyamide 66, with glass fiber and PTFE, 8-mm-granulate
- Sibur TVERPET® Polyethylene Terephthalate (PET)
- Covestro Bayflex® XGT-100 Polyurethane Elastomeric RIM, MDI-based 2-Component Liquid System
- Hippe PF CP 203 Cellulose Paper Reinforced Phenolic Resin - Sheet
- A. Schulman ComAlloy Voloy® 431 Glass/Mineral Reinforced, PET Alloy, Flame Retardant, UL
Copyright © lookpolymers.com All Rights Reserved