- Nilit FRIANYL A63 SG-GV 1515 Nylon 6.6 for injection molding, 15% mineral filled and 15% glass fiber reinforced
Nilit FRIANYL A63 SG-GV 1515 Nylon 6.6 for injection molding, 15% mineral filled and 15% glass fiber reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL A63 SG-GV 1515 Nylon 6.6 for injection molding, 15% mineral filled and 15% glass fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Water Absorption | 1.4 - 2.1 % | 1.4 - 2.1 % | ISO 62 |
| Water Absorption at Saturation | 6.0 - 8.0 % | 6.0 - 8.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0050 - 0.015 cm/cm | 0.0050 - 0.015 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 170 MPa | 24700 psi | ISO 2039-1 |
| Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527 |
| Tensile Modulus | 6.50 GPa | 943 ksi | ISO 527 |
| Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 |
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | DIN 53453 |
| 4.00 J/cm² @Temperature -40.0 °C |
19.0 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 120 °C | 248 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- Plaskolite West Optix® CA-81 General Purpose Acrylic Resin
- REXtac Rextac® RT 2315 Amorphous Polyalphaolefin (APAO)
- Quadrant EPP Semitron® ESd 490HR Static dissipative PEEK for use in test fixtures. Non-sloughing and low moisture absorption. (ASTM Product Data Sheet)
- Pasargad Polymer Peyvand Pasamid 3P-H1130B Nylon 6, 30% Glass Fiber Reinforced
- KB Alloys Ticar® 3% Ti - 0.3% C Titanium Carbon Aluminum Rod
- Gwent Electronic Materials C2090415D1 Gold Ink
- Global PP-2311-SC Polypropylene Block Copolymer
- Polyram RamOfin PPH343T4BK10 Polypropylene, 20% Mineral Filled
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane, 310ºF Cure Temperature
- PlastxWorld CEVIAN®-V 320 ABS
Copyright © lookpolymers.com All Rights Reserved