- Nilit FRIANYL A63 KG20 Nylon 6.6 for injection molding, 20% chalk filled
Nilit FRIANYL A63 KG20 Nylon 6.6 for injection molding, 20% chalk filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL A63 KG20 Nylon 6.6 for injection molding, 20% chalk filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection molding (low warpage and good form stability).Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ISO 1183 |
| Water Absorption | 1.5 - 2.5 % | 1.5 - 2.5 % | ISO 62 |
| Water Absorption at Saturation | 6.0 - 8.0 % | 6.0 - 8.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.010 - 0.025 cm/cm | 0.010 - 0.025 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 141 MPa | 20500 psi | ISO 2039-1 |
| Tensile Strength at Break | 65.0 MPa | 9430 psi | ISO 527 |
| Elongation at Break | 15 % | 15 % | ISO 527 |
| Tensile Modulus | 3.60 GPa | 522 ksi | ISO 527 |
| Flexural Strength | 75.0 MPa | 10900 psi | ISO 178 |
| Flexural Modulus | 2.90 GPa | 421 ksi | ISO 178 |
| Charpy Impact Unnotched | NB | NB | DIN 53453 |
| NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.450 J/cm² | 2.14 ft-lb/in² | DIN 53453 |
| 0.400 J/cm² @Temperature -40.0 °C |
1.90 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- Okulen® 1000 - REG PE Colored
- Polimeri Europa Sinkral® F 332 ABS Resin
- SABIC Innovative Plastics LNP THERMOCOMP LF005 PEEK
- SABIC Innovative Plastics LNP THERMOCOMP RF008XXH PA 66
- Denka VINYKON S210040 PVC, S grade for transparent extrusion molding
- DuPont Teijin Films Mylar® RSX951 Polyester Film, 140 Gauge
- Asahi Kasei Thermylene® P6-20FG-1812 20% Glass Fiber Reinforced, UV Stabilized
- Ineos ABS Lustran® QE 1122, Injection Grade (discontinued **)
Copyright © lookpolymers.com All Rights Reserved