Nilit FRIANYL A63 H-SG40 Nylon 6.6 for injection molding, 40% mineral filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL A63 H-SG40 Nylon 6.6 for injection molding, 40% mineral filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection molding, heat stabilized (dark natural color).Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 |
| Water Absorption | 1.5 - 2.0 % | 1.5 - 2.0 % | ISO 62 |
| Water Absorption at Saturation | 6.0 - 8.0 % | 6.0 - 8.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0050 - 0.015 cm/cm | 0.0050 - 0.015 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 162 MPa | 23500 psi | ISO 2039-1 |
| Tensile Strength at Break | 64.0 MPa | 9280 psi | ISO 527 |
| Tensile Modulus | 4.10 GPa | 595 ksi | ISO 527 |
| Flexural Strength | 60.0 MPa | 8700 psi | ISO 178 |
| Flexural Modulus | 3.60 GPa | 522 ksi | ISO 178 |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | DIN 53453 |
| 2.20 J/cm² @Temperature -40.0 °C |
10.5 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 130 °C | 266 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 600 V | 600 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- Reliance Industries 67-11 Polyvinyl Chloride
- NOVA Chemicals Sclair® 14L1 Octene LMDPE Film Resin (discontinued **)
- Flint Hills P4C6B-194 Polypropylene Homopolymer
- LG Chemical Lupox® HI2100M PBT+GF10%
- Karina 752D48/1-C-IS-BZ Black PVC Compound
- Multibase Multi-Flex® A 5500 MR Natural TPE Thermoplastic Elastomer
- Cytec Cyply® 1002 Epoxy Fiberglass Composite, Isotropic
- Fainplast Compounds GSO 70/33 Flexible PVC, Injection Molding for Footwear
- Multibase Multibatch® MP 52518 BOPP White Pearlised Film
- Samyang Triloy® S460G15 Polymer Alloy, Reinforced
Copyright © lookpolymers.com All Rights Reserved