Sax Polymers SAXAMID 236Q33 Nylon 6.6, Impact Modified

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade
Manufacturer	Sax Polymers
Trade Name	SAXAMID
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Sax Polymers SAXAMID 236Q33 Nylon 6.6, Impact Modified.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

SAXAMID 236Q33 is a impact-modified polyamide 6.6 injection-molding-grade with very good flow properties and outstanding toughness. Even at low temperatures this grade offers super-tough properties.Information provided by SAX Polymers

Physical Properties	Metric	English	Comments
Density	1.10 g/cc	0.0397 lb/in³	ISO 1183
Viscosity Test	150 cm³/g	150 cm³/g	H<sub>2</sub>SO<sub>4</sub>; ISO 307

Mechanical Properties	Metric	English	Comments
Tensile Strength	40.0 MPa	5800 psi	5 mm/min; ISO 527-1
Elongation at Break	10 %	10 %	5 mm/min; ISO 527-1
Tensile Modulus	1.50 GPa	218 ksi	1 mm/min; ISO 527-1
Flexural Strength	64.0 MPa	9280 psi	2 mm/min; ISO 178
Flexural Modulus	1.60 GPa	232 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	23.0 kJ/m² @Temperature -30.0 °C	10.9 ft-lb/in² @Temperature -22.0 °F	ISO 180/1A
	90.0 kJ/m² @Temperature 23.0 °C	42.8 ft-lb/in² @Temperature 73.4 °F	ISO 180/1A
Izod Impact, Unnotched (ISO)	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 180/1U
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	ISO 180/1U
Charpy Impact Unnotched	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179/1eU
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	ISO 179/1eU
Charpy Impact, Notched	2.10 J/cm² @Temperature -30.0 °C	9.99 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
	9.00 J/cm² @Temperature 23.0 °C	42.8 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	65.0 °C	149 °F	80104 s=60mm; ISO 75-1 a
Vicat Softening Point	180 °C	356 °F	B/120; ISO 306

Processing Properties	Metric	English
Melt Temperature	270 - 300 °C	518 - 572 °F
Mold Temperature	70.0 - 90.0 °C	158 - 194 °F
Drying Temperature	80.0 °C @Time 7200 - 21600 sec	176 °F @Time 2.00 - 6.00 hour
Moisture Content	<= 0.20 %	<= 0.20 %