Ineos ABS Lustran® 356 Extrusion, Low-Gloss (discontinued **)
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® 356 Extrusion, Low-Gloss
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Properties tested in transverse direction (worst case) on 125-mil (3.2 mm) extruded sheets specimens with
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D792 |
| Melt Flow | 7.0 g/10 min @Load 10.0 kg, Temperature 230 °C |
7.0 g/10 min @Load 22.0 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | ASTM D638 |
| Tensile Modulus | 2.10 GPa | 305 ksi | ASTM D638 |
| Flexural Yield Strength | 47.6 MPa | 6900 psi | ASTM D790 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ASTM D790 |
| Izod Impact, Notched | 1.30 J/cm @Thickness 3.17 mm |
2.44 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| 0.500 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
0.937 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 | |
| Impact Test | 31.0 J @Thickness 2.50 mm |
22.9 ft-lb @Thickness 0.0984 in |
Instrumented Impact, Total Energy; 2.5 mm thick, 7.6 mph, 3 in. clamp, 0.5 in. dart; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 83.0 µm/m-°C @Temperature 20.0 °C |
46.1 µin/in-°F @Temperature 68.0 °F |
Injection molded sample; ASTM D696 |
| UL RTI, Electrical | 60.0 °C @Thickness 1.60 mm |
140 °F @Thickness 0.0630 in |
UL746B |
| UL RTI, Mechanical with Impact | 60.0 °C @Thickness 1.60 mm |
140 °F @Thickness 0.0630 in |
UL746B |
| UL RTI, Mechanical without Impact | 60.0 °C @Thickness 1.60 mm |
140 °F @Thickness 0.0630 in |
UL746B |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
|
| HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 25 % | 25 % | 60°; Sheet; ASTM D523 |
| Transmission, Visible | 0.00 % | 0.00 % | Opaque only |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 215 - 240 °C | 419 - 464 °F |
Users viewing this material also viewed the following:
- Chevron Phillips Dynex™ D605A6 Enhanced LLDPE Blown Film Resin (discontinued **)
- Hong Kun Group CDI Pharmaceutical Intermediate
- LATI Laticonther 52/11 GR/70 PP Homopolymer
- LATI Latimass 82-02 D030 PA12
- Styron Magnumâ„¢ 3513 Acrylonitrile Butadiene Styrene (ABS)
- CPC - Vycom FLAMETEC™ CPVC Chlorinated Polyvinyl Chloride Sheet
- ChevronTexaco Texcool® EXL 304
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 30A, Black Sulfur Cure
- Kazanorgsintez PE2NT 11-285 High Density Polyethylene Composite
Copyright © lookpolymers.com All Rights Reserved