Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.18 g/cc | 1.18 g/cc | ISO 1183 |
Linear Mold Shrinkage | 0.010 - 0.030 cm/cm | 0.010 - 0.030 in/in | |
Melt Flow | 19 g/10 min @Load 10.0 kg, Temperature 190 °C |
19 g/10 min @Load 22.0 lb, Temperature 374 °F |
ISO 1133 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Hardness, Shore A | 63 | 63 | ISO 868 |
Tensile Strength | 6.30 MPa | 914 psi | ISO 37 |
Tensile Strength, Ultimate | 2.80 MPa | 406 psi | ISO 37 |
Elongation at Break | 480 % | 480 % | ISO 37 |
Flexural Strength | 2.30 MPa | 334 psi | ISO 178 |
Flexural Modulus | 0.0233 GPa | 3.38 ksi | ISO 178 |
Tear Strength | 27.8 kN/m | 159 pli | ISO 34 |
Taber Abrasion, mg/1000 Cycles | 95 | 95 | ASTM D3389 |
Compression Set | 20 % @Temperature 23.0 °C, Time 79200 sec |
20 % @Temperature 73.4 °F, Time 22.0 hour |
ISO 815 |
72 % @Temperature 70.0 °C, Time 79200 sec |
72 % @Temperature 158 °F, Time 22.0 hour |
ISO 815 |
Processing Properties | Metric | English | Comments |
---|---|---|---|
Feed Temperature | 165 - 175 °C | 329 - 347 °F | |
Middle Barrel Temperature | 170 - 180 °C | 338 - 356 °F | |
Front Barrel Temperature | 180 - 195 °C | 356 - 383 °F | |
Nozzle Temperature | 185 - 200 °C | 365 - 392 °F | |
Melt Temperature | 195 °C | 383 °F | |
Mold Temperature | 20.0 - 40.0 °C | 68.0 - 104 °F | |
Drying Temperature | 65.0 - 80.0 °C | 149 - 176 °F | |
Dry Time | 2 - 4 hour | 2 - 4 hour |
Descriptive Properties | Value | Comments |
---|---|---|
Injection Speed | MED-FAST |