ExxonMobil Exact™ 9061 Ethylene-based Plastomer Resin

Category	Polymer , Thermoplastic , Elastomer, TPE
Manufacturer	Exxon Chemical
Trade Name	EXACT™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Exact™ 9061 Ethylene-based Plastomer Resin.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Product Description: Exact 9061 plastomer is an ethylene butene copolymer produced using ExxonMobil Chemical's EXXPOL™ Technology, exhibiting both plastic and elastomeric properties.Key Features:PP/TPO modification.EVA modification.Designed as a low density and high molecular weight polymer modifier to impart impact strength and toughness.Available as free flowing pellets.Availability: Africa & Middle East, Europe, North America, Asia Pacific, Latin America and South America.All physical properties were measured from specimens cut from compression molded plaques per ASTM D 4703, Procedure A, Type I and conditioned at 23°C for a minimum of 40 hours per ASTM D 618 prior to testing. All stress/strain tests used specimens cut with a Type IV (Die C) die and tested with a grip separation of 25 mm (1") and a crosshead speed of 20 in./min.Information provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Specific Gravity	0.862 g/cc	0.862 g/cc	ASTM D1505
Melt Flow	0.50 g/10 min @Load 2.16 kg, Temperature 190 °C	0.50 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
	0.50 g/10 min @Load 2.16 kg, Temperature 190 °C	0.50 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	59 @Time 15.0 sec	59 @Time 0.00417 hour	0.08 in; ASTM D2240
Tensile Strength at Break	2.40 MPa	348 psi	ASTM D412 and ISO 37
Tensile Stress	1.70 MPa @Strain 100 %	247 psi @Strain 100 %	ASTM D412 and ISO 37
Elongation at Break	1200 %	1200 %	ASTM D412 and ISO 37
Flexural Modulus, 1% Secant	6.50 MPa	943 psi	ASTM D790 and ISO 178

Thermal Properties	Metric	English	Comments
Heat of Fusion	41.0 J/g	17.6 BTU/lb	Crystallinity; ExxonMobil Method
Melting Point	41.0 °C	106 °F	Peak; ExxonMobil Method
Crystallization Temperature	29.0 °C	84.2 °F	ExxonMobil Method
Vicat Softening Point	47.0 °C	117 °F	ASTM D1525 and ISO 306/A
Glass Transition Temp, Tg	-49.0 °C	-56.2 °F	ExxonMobil Method